Influence Of Non-Metallic Inclusions On The High Cycle Fatigue Strength Of Steels
Published 2021 View Full Article
- Home
- Publications
- Publication Search
- Publication Details
Title
Influence Of Non-Metallic Inclusions On The High Cycle Fatigue Strength Of Steels
Authors
Keywords
Non-metallic inclusions, High strength steel, Fatigue strength, Infinite life, AISI 4140 steel
Journal
INTERNATIONAL JOURNAL OF FATIGUE
Volume -, Issue -, Pages 106553
Publisher
Elsevier BV
Online
2021-09-20
DOI
10.1016/j.ijfatigue.2021.106553
References
Ask authors/readers for more resources
Related references
Note: Only part of the references are listed.- Roles of microstructure, inclusion, and surface roughness on rolling contact fatigue of a wind turbine gear
- (2020) Hao Zhou et al. FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES
- Effect of superimposed compressive stresses on rolling contact fatigue initiation at hard and soft inclusions
- (2020) Hamidreza Mahdavi et al. INTERNATIONAL JOURNAL OF FATIGUE
- A pragmatic approach to predict fatigue strength concerning the short crack behavior in VHCF
- (2020) Kepeng Sun et al. INTERNATIONAL JOURNAL OF FATIGUE
- Multiaxial fatigue assessment of steels with non-metallic inclusions by means of adapted critical plane criteria
- (2020) Pedro Vinícius Sousa Machado et al. THEORETICAL AND APPLIED FRACTURE MECHANICS
- Finite element study of cyclic plasticity near a subsurface inclusion under rolling contact and macro-residual stresses
- (2020) Hamidreza Mahdavi et al. INTERNATIONAL JOURNAL OF FATIGUE
- Crack initiation and life estimation for 316 and 430 stainless steel specimens by means of a critical plane approach
- (2020) Sabrina Vantadori et al. INTERNATIONAL JOURNAL OF FATIGUE
- Fatigue life analysis of wind turbine gear with oxide inclusion
- (2020) Ran Liu et al. FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES
- Prediction of spatial distribution of the composition of inclusions on the entire cross section of a linepipe steel continuous casting slab
- (2020) Qiang Ren et al. JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY
- Subsurface Crack Propagation from Internal Defect in Rolling Contact Fatigue of Railway Wheel Steel
- (2020) Takanori Kato et al. MATERIALS TRANSACTIONS
- Notch fatigue life estimation of Ti-6Al-4V
- (2020) Camilla Ronchei et al. ENGINEERING FAILURE ANALYSIS
- Broad review of “White Etching Crack” failure in wind turbine gearbox bearings: Main factors and experimental investigations
- (2020) Fernando José López-Uruñuela et al. INTERNATIONAL JOURNAL OF FATIGUE
- Influence of steel cleanliness and heat treatment conditions on rolling contact fatigue of 100Cr6
- (2019) M. Oezel et al. WEAR
- A new proposed Weibull distribution of inclusion size and its correlation with rolling contact fatigue life of an extra clean bearing steel
- (2019) Zhaoxi Cao et al. INTERNATIONAL JOURNAL OF FATIGUE
- Material defects as cause for the fatigue failure of metallic components
- (2019) U. Zerbst et al. INTERNATIONAL JOURNAL OF FATIGUE
- Detection and analysis of magnetic particle testing defects on heavy truck crankshaft manufactured by microalloyed medium-carbon forging steel
- (2019) Jin-long Lu et al. JOURNAL OF IRON AND STEEL RESEARCH INTERNATIONAL
- Effect of Non-Metallic Inclusion Chemical and Phase Composition on Corrosion Resistance of Carbon and Low Alloy Steels in Water Media Typical for Oilfield Pipeline Operating Conditions
- (2019) A. V. Amezhnov et al. METALLURGIST
- Finite element simulation of subsurface initiated damage from non-metallic inclusions in wind turbine gearbox bearings
- (2019) Hamza A. Al-Tameemi et al. INTERNATIONAL JOURNAL OF FATIGUE
- Embrittlement of welded joints of tram rails in city environments
- (2018) M. Kawiak et al. ENGINEERING FAILURE ANALYSIS
- Evaluation of high-cycle bending fatigue and fracture behaviors in EN-GJS700-2 ductile cast iron of crankshafts
- (2018) Mohammad Jamalkhani Khameneh et al. ENGINEERING FAILURE ANALYSIS
- Microstructural analysis and fatigue fracture behavior of rail steel
- (2018) Reza Masoudi Nejad et al. MECHANICS OF ADVANCED MATERIALS AND STRUCTURES
- Initiation of sub-surface micro-cracks and white etching areas from debonding at non-metallic inclusions in wind turbine gearbox bearing
- (2018) H.A. Al-Tameemi et al. WEAR
- Failure analysis of four-cylinder diesel engine crankshaft
- (2018) K. Aliakbari Journal of the Brazilian Society of Mechanical Sciences and Engineering
- Synergistic action of hydrogen gas and weld defects on fracture toughness of X80 pipeline steel
- (2018) Teng An et al. INTERNATIONAL JOURNAL OF FATIGUE
- Estimation of fatigue life under multiaxial loading by varying the critical plane orientation
- (2017) Andrea Carpinteri et al. INTERNATIONAL JOURNAL OF FATIGUE
- An updated review: white etching cracks (WECs) and axial cracks in wind turbine gearbox bearings
- (2016) M.-H. Evans MATERIALS SCIENCE AND TECHNOLOGY
- Formation of white etching cracks at manganese sulfide (MnS) inclusions in bearing steel due to hammering impact loading
- (2016) T. Bruce et al. WIND ENERGY
- Critical Plane Orientation Influence on Multiaxial High-Cycle Fatigue Assessment
- (2015) A. Carpinteri et al. Physical Mesomechanics
- Critical Plane Orientation Influence on Multiaxial High-Cycle Fatigue Assessment
- (2015) A. Carpinteri et al. Physical Mesomechanics
- Multiaxial high cycle fatigue threshold with small defects and cracks
- (2014) K. Yanase et al. ENGINEERING FRACTURE MECHANICS
- On the characterization of the critical plane with a simple and fast alternative measure of the shear stress amplitude in multiaxial fatigue
- (2011) J.A. Araújo et al. INTERNATIONAL JOURNAL OF FATIGUE
- Transition of fatigue failure mode of Ni–Cr–Mo low-alloy steel in very high cycle regime
- (2009) K. Shiozawa et al. INTERNATIONAL JOURNAL OF FATIGUE
- Marine main engine crankshaft failure analysis: A case study
- (2008) M. Fonte et al. ENGINEERING FAILURE ANALYSIS
- Very high cycle fatigue properties of bearing steel under axial loading condition
- (2008) K. Shiozawa et al. INTERNATIONAL JOURNAL OF FATIGUE
Find the ideal target journal for your manuscript
Explore over 38,000 international journals covering a vast array of academic fields.
SearchCreate your own webinar
Interested in hosting your own webinar? Check the schedule and propose your idea to the Peeref Content Team.
Create Now