Journal
MATERIALS LETTERS
Volume 101, Issue -, Pages 72-75Publisher
ELSEVIER
DOI: 10.1016/j.matlet.2013.03.079
Keywords
Semiconductors; Defects
Ask authors/readers for more resources
Silicon carbide (SiC) is an attractive wide band gap IV-IV semiconductor material suitable for high temperature, voltage and frequency applications. However, the presence of defects and its identification is the major issue prior to using for electronic devices application. To identify the defects, an easy and quick method is highly desirable. The present study has investigated molten KOH etching of 6H n-SiC for revealing of defects as a function of temperature (400-600) degrees C and time. The etch pits were observed using Nomarski microscope and categorized with respect to their morphology. Result revealed that 500 degrees C was the optimum temperature for identification of micropipes (mu P), screw dislocation (SD), threading edge dislocation (TD) and basal plane dislocation (BD). The etch pit and micropipe density were found in the range of similar to 1 x 10(4) cm(-2) and (8-10) cm(-2) respectively. Also, the etching rate was found to obey an Arrhenius law with activation energy of (19-21) kcal/mol. (C) 2013 Elsevier B.V. All rights reserved.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available