Laser-induced surface activation of biocomposites for electroless metallization

In this work biocomposites containing polylactide (PLA), polycaprolactone (PCL), copper(II) oxide and copper acetylacetonate were manufactured by an extrusion process. The extruded composites differed with respect to the PLA/PCL ratio whereas the content of mixed copper(II) oxide and copper acetylacetonate powders was held constant at 20 wt%. The main aims for the addition of PCL was to increase impact strength resistance, improve surface catalytic properties and reduce the temperature of extrusion, thus limiting degradation effects initiated by copper acetylacetonate. The composite samples were irradiated with an ArF excimer laser varying the number of laser pulses and then metalized by electroless plating. Based on optical microscopy, scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDX) and X-ray photoelectron spectroscopy (XPS) measurements, it was found that (i) PCL was dispersed in the form of droplets in all volume of PLA, (ii) the copper compounds were preferably located in the dispersed PCL phase, and (iii) composites with higher PCL content were more effectively metalized. (C) 2016 Elsevier B.V. All rights reserved.