Combined impact of elastic stress, prestrain and electrochemical charging on the hydrogen-induced cracking of high-strength steel
Published 2023 View Full Article
- Home
- Publications
- Publication Search
- Publication Details
Title
Combined impact of elastic stress, prestrain and electrochemical charging on the hydrogen-induced cracking of high-strength steel
Authors
Keywords
-
Journal
INTERNATIONAL JOURNAL OF HYDROGEN ENERGY
Volume -, Issue -, Pages -
Publisher
Elsevier BV
Online
2023-01-19
DOI
10.1016/j.ijhydene.2023.01.040
References
Ask authors/readers for more resources
Related references
Note: Only part of the references are listed.- In-situ 3D observation of hydrogen-assisted particle damage behavior in 7075 Al alloy by synchrotron X-ray tomography
- (2022) Yafei Wang et al. ACTA MATERIALIA
- Suppressed hydrogen embrittlement of high-strength Al alloys by Mn-rich intermetallic compound particles
- (2022) Yuantao Xu et al. ACTA MATERIALIA
- Quantitative assessment of the hydrogen induced cracking for 2.25Cr-1Mo-0.25V steel under electrochemical charging conditions
- (2021) Y.F. Wang et al. ENGINEERING FAILURE ANALYSIS
- Structures of hydrogen-induced cracks under different hydrogen concentrations for a high strength steel
- (2021) Y.F. Wang et al. ENGINEERING FAILURE ANALYSIS
- Investigation of the hydrogen induced cracking behaviour of API 5L X65 pipeline steel
- (2020) Tonye Alaso Jack et al. INTERNATIONAL JOURNAL OF HYDROGEN ENERGY
- Pre-strain effects on critical stress and hydrogen content for hydrogen-induced quasi-cleavage fracture in a TRIP-aided bainitic ferrite steel: Martensitic transformation, matrix damage, and strain aging
- (2020) Bakuya Kumai et al. INTERNATIONAL JOURNAL OF HYDROGEN ENERGY
- Comprehensive study on hydrogen induced cracking of electrical resistance welded API X52 pipeline steel
- (2020) A.A. Khalili Tabas et al. INTERNATIONAL JOURNAL OF HYDROGEN ENERGY
- Improved hydrogen embrittlement resistance after quenching–tempering treatment for a Cr-Mo-V high strength steel
- (2019) Yafei Wang et al. INTERNATIONAL JOURNAL OF HYDROGEN ENERGY
- EBSD characterization of hydrogen induced blisters and internal cracks in TRIP-assisted steel
- (2019) A. Laureys et al. MATERIALS CHARACTERIZATION
- Ab initio simulation of hydrogen-induced decohesion in cementite-containing microstructures
- (2018) Eunan J. McEniry et al. ACTA MATERIALIA
- Hydrogen induced cracking of pipeline and pressure vessel steels: A review
- (2018) Goutam Ghosh et al. ENGINEERING FRACTURE MECHANICS
- Hydrogen trapping and hydrogen induced cracking of welded X100 pipeline steel in H 2 S environments
- (2018) Lijun Gan et al. INTERNATIONAL JOURNAL OF HYDROGEN ENERGY
- A focus on different factors affecting hydrogen induced cracking in oil and natural gas pipeline steel
- (2017) M.A. Mohtadi-Bonab et al. ENGINEERING FAILURE ANALYSIS
- Hydrogen bubble nucleation in α-iron
- (2017) W.T. Geng et al. SCRIPTA MATERIALIA
- Crack and blister initiation and growth in purified iron due to hydrogen loading
- (2016) Marie C. Tiegel et al. ACTA MATERIALIA
- Investigation of the effect of electrolytic hydrogen charging of X70 steel: II. Microstructural and crystallographic analyses of the formation of hydrogen induced cracks and blisters
- (2016) A.A. Saleh et al. INTERNATIONAL JOURNAL OF HYDROGEN ENERGY
- Hydrogen Embrittlement Understood
- (2015) Ian M. Robertson et al. METALLURGICAL AND MATERIALS TRANSACTIONS B-PROCESS METALLURGY AND MATERIALS PROCESSING SCIENCE
- A comparative study of hydrogen induced cracking behavior in API 5L X60 and X70 pipeline steels
- (2013) M.A. Mohtadi-Bonab et al. ENGINEERING FAILURE ANALYSIS
- An effective finite element model for the prediction of hydrogen induced cracking in steel pipelines
- (2012) Abderrazak Traidia et al. INTERNATIONAL JOURNAL OF HYDROGEN ENERGY
- Validation of void growth models using X-ray microtomography characterization of damage in dual phase steels
- (2011) C. Landron et al. ACTA MATERIALIA
- Internal and surface damage of multiphase steels and pure iron after electrochemical hydrogen charging
- (2011) D. Pérez Escobar et al. CORROSION SCIENCE
- Recent developments in the study of hydrogen embrittlement: Hydrogen effect on dislocation nucleation
- (2010) Afrooz Barnoush et al. ACTA MATERIALIA
- Effect of non-metallic inclusions on hydrogen-induced cracking of API5L X100 steel
- (2010) T.Y. Jin et al. INTERNATIONAL JOURNAL OF HYDROGEN ENERGY
- Revisiting hydrogen embrittlement models and hydrogen-induced homogeneous nucleation of dislocations
- (2009) Reiner Kirchheim SCRIPTA MATERIALIA
Publish scientific posters with Peeref
Peeref publishes scientific posters from all research disciplines. Our Diamond Open Access policy means free access to content and no publication fees for authors.
Learn MoreCreate your own webinar
Interested in hosting your own webinar? Check the schedule and propose your idea to the Peeref Content Team.
Create Now