Structures of hydrogen-induced cracks under different hydrogen concentrations for a high strength steel
Published 2021 View Full Article
- Home
- Publications
- Publication Search
- Publication Details
Title
Structures of hydrogen-induced cracks under different hydrogen concentrations for a high strength steel
Authors
Keywords
Steel, Hydrogen-induced cracking, Structure, Pressure vessel
Journal
ENGINEERING FAILURE ANALYSIS
Volume 128, Issue -, Pages 105587
Publisher
Elsevier BV
Online
2021-07-08
DOI
10.1016/j.engfailanal.2021.105587
References
Ask authors/readers for more resources
Related references
Note: Only part of the references are listed.- Crack propagation rate of hydrogen-induced cracking in high sulfur-containing pipelines
- (2021) Shaohua Dong et al. ENGINEERING FAILURE ANALYSIS
- Corrigendum to “Quantitative assessment of the hydrogen induced cracking for 2.25Cr-1Mo-0.25V steel under electrochemical charging conditions” [Eng. Fail. Anal. 124 (2021) 105343]
- (2021) Y.F. Wang et al. ENGINEERING FAILURE ANALYSIS
- Ductile failure of flat plates containing two through-wall cracks: Experimental investigation and numerical modeling
- (2021) Xue-Wei Zhang et al. INTERNATIONAL JOURNAL OF PRESSURE VESSELS AND PIPING
- Electrochemical hydrogen charging to simulate hydrogen flaking in pressure vessel steels
- (2019) A. Laureys et al. ENGINEERING FRACTURE MECHANICS
- Improved hydrogen embrittlement resistance after quenching–tempering treatment for a Cr-Mo-V high strength steel
- (2019) Yafei Wang et al. INTERNATIONAL JOURNAL OF HYDROGEN ENERGY
- Failure investigation of hydrogen induced cracking of stabilator skin in jet aircraft
- (2018) Bokwon Lee et al. ENGINEERING FAILURE ANALYSIS
- The detrimental effect of hydrogen at dislocations on the hydrogen embrittlement susceptibility of Fe-C-X alloys: An experimental proof of the HELP mechanism
- (2018) T. Depover et al. INTERNATIONAL JOURNAL OF HYDROGEN ENERGY
- The evolutions of microstructure and mechanical properties of 2.25Cr-1Mo-0.25V steel with different initial microstructures during tempering
- (2017) Zhonghua Jiang et al. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
- Crack and blister initiation and growth in purified iron due to hydrogen loading
- (2016) Marie C. Tiegel et al. ACTA MATERIALIA
- Hydrogen induced cold cracking of creep resistant ferritic P91 steel for different diffusible hydrogen levels in deposited metal
- (2016) Chandan Pandey et al. INTERNATIONAL JOURNAL OF HYDROGEN ENERGY
- Investigation of the effect of electrolytic hydrogen charging of X70 steel: II. Microstructural and crystallographic analyses of the formation of hydrogen induced cracks and blisters
- (2016) A.A. Saleh et al. INTERNATIONAL JOURNAL OF HYDROGEN ENERGY
- Microstructural characterization of hydrogen induced cracking in TRIP-assisted steel by EBSD
- (2016) A. Laureys et al. MATERIALS CHARACTERIZATION
- Bulk Diffusion-Controlled Thermal Desorption Spectroscopy with Examples for Hydrogen in Iron
- (2015) Reiner Kirchheim METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE
- Failure Analysis of Weld Cracking in a Thick-Walled 2.25Cr-1Mo Steel Pressure Vessel
- (2014) Xiaowei Lei et al. JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE
- An effective finite element model for the prediction of hydrogen induced cracking in steel pipelines
- (2012) Abderrazak Traidia et al. INTERNATIONAL JOURNAL OF HYDROGEN ENERGY
- Internal and surface damage of multiphase steels and pure iron after electrochemical hydrogen charging
- (2011) D. Pérez Escobar et al. CORROSION SCIENCE
- Transient hydrogen diffusion analyses coupled with crack-tip plasticity under cyclic loading
- (2008) Hirokazu Kotake et al. INTERNATIONAL JOURNAL OF PRESSURE VESSELS AND PIPING
Find the ideal target journal for your manuscript
Explore over 38,000 international journals covering a vast array of academic fields.
SearchCreate your own webinar
Interested in hosting your own webinar? Check the schedule and propose your idea to the Peeref Content Team.
Create Now