Defect-induced cracking and fine granular characteristics in very-high-cycle fatigue of laser powder bed fusion AlSi10Mg alloy
Published 2022 View Full Article
- Home
- Publications
- Publication Search
- Publication Details
Title
Defect-induced cracking and fine granular characteristics in very-high-cycle fatigue of laser powder bed fusion AlSi10Mg alloy
Authors
Keywords
Laser powder bed fusion, Very-high-cycle fatigue, Defect-induced crack, Grain refinement, Misorientation
Journal
INTERNATIONAL JOURNAL OF FATIGUE
Volume 158, Issue -, Pages 106770
Publisher
Elsevier BV
Online
2022-01-29
DOI
10.1016/j.ijfatigue.2022.106770
References
Ask authors/readers for more resources
Related references
Note: Only part of the references are listed.- 3D short fatigue crack closure behavior in Ti-6Al-4V alloy investigated using in-situ high resolution synchrotron X-ray tomography
- (2021) Valary Tubei et al. ENGINEERING FRACTURE MECHANICS
- The effect of defect population on anisotropic fatigue resistance of selective laser melted AlSi10Mg alloy
- (2021) Z.K. Wu et al. INTERNATIONAL JOURNAL OF FATIGUE
- A comparative investigation on the microstructure and mechanical properties of additively manufactured aluminum alloys
- (2021) Muztahid Muhammad et al. INTERNATIONAL JOURNAL OF FATIGUE
- Fracture resistance of AlSi10Mg fabricated by laser powder bed fusion
- (2021) Moses J. Paul et al. ACTA MATERIALIA
- Fine granular area formation by damage‐induced shear strain localization in very‐high‐cycle fatigue
- (2021) Huan‐Jie Zhang et al. FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES
- High cycle fatigue in selective laser melted Ti-6Al-4V
- (2020) Punit Kumar et al. ACTA MATERIALIA
- Microstructure refinement and grain size distribution in crack initiation region of very-high-cycle fatigue regime for high-strength alloys
- (2020) Yukun Chang et al. INTERNATIONAL JOURNAL OF FATIGUE
- Composition-dependent dynamic precipitation and grain refinement in Al-Si system under high-pressure torsion
- (2020) Shenbao Jin et al. JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY
- Microstructure effects on fatigue crack growth in additively manufactured Ti–6Al–4V
- (2020) Raeann VanSickle et al. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
- Defects as a root cause of fatigue weakening of additively manufactured AlSi10Mg components
- (2020) Paolo Ferro et al. THEORETICAL AND APPLIED FRACTURE MECHANICS
- Fatigue strength assessment of “as built” AlSi10Mg manufactured by SLM with different build orientations
- (2020) S. Beretta et al. INTERNATIONAL JOURNAL OF FATIGUE
- Effects of inclusion size and stress ratio on the very-high-cycle fatigue behavior of pearlitic steel
- (2020) Tao Cong et al. INTERNATIONAL JOURNAL OF FATIGUE
- A survey of fatigue properties from wrought and additively manufactured Ti-6Al-4V
- (2020) Jeremy H. Rao et al. MATERIALS LETTERS
- Crack initiation behavior and fatigue performance up to very-high-cycle regime of AlSi10Mg fabricated by selective laser melting with two powder sizes
- (2020) Z.M. Jian et al. INTERNATIONAL JOURNAL OF FATIGUE
- Subsurface faceted cracking behavior of selective laser melting Ni-based superalloy under very high cycle fatigue
- (2020) Wei Li et al. SCRIPTA MATERIALIA
- Nanograin formation in dimple ridges due to local severe-plastic-deformation during ductile fracture
- (2020) Xiangnan Pan et al. SCRIPTA MATERIALIA
- A generalized criterion for fatigue crack growth in additively manufactured materials – Build orientation and geometry effects
- (2020) M.M. Mirsayar INTERNATIONAL JOURNAL OF FATIGUE
- High-cycle and very-high-cycle fatigue behaviour of a titanium alloy with equiaxed microstructure under different mean stresses
- (2019) Xiangnan Pan et al. FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES
- Initiation and growth behaviour of small internal fatigue cracks in Ti-6Al-4V via synchrotron radiation microcomputed tomography
- (2019) Fumiyoshi Yoshinaka et al. FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES
- The formation of discontinuous gradient regimes during crack initiation in high strength steels under very high cycle fatigue
- (2019) Chengqi Sun et al. INTERNATIONAL JOURNAL OF FATIGUE
- Influence of Si precipitates on fracture mechanisms of AlSi10Mg parts processed by Selective Laser Melting
- (2019) J. Delahaye et al. ACTA MATERIALIA
- Influence of the annealing and defects on the VHCF behavior of an SLM AlSi10Mg alloy
- (2019) Andrea Tridello et al. FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES
- In situ synchrotron ultrasonic fatigue testing device for 3D characterisation of internal crack initiation and growth
- (2019) Alexandre Messager et al. FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES
- Fatigue life and mechanistic modeling of interior micro-defect induced cracking in high cycle and very high cycle regimes
- (2018) Ming-Liang Zhu et al. ACTA MATERIALIA
- Fatigue properties of AlSi10Mg obtained by additive manufacturing: Defect-based modelling and prediction of fatigue strength
- (2018) S. Romano et al. ENGINEERING FRACTURE MECHANICS
- FGA formation mechanism for X10CrNiMoV12-2-2 and 34CrNiMo6 for constant and variable amplitude tests under the influence of applied mean loads
- (2018) F. Ritz et al. FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES
- Predicting the 3D fatigue crack growth rate of small cracks using multimodal data via Bayesian networks: In-situ experiments and crystal plasticity simulations
- (2018) Andrea Rovinelli et al. JOURNAL OF THE MECHANICS AND PHYSICS OF SOLIDS
- Fatigue crack growth anisotropy, texture and residual stress in austenitic steel made by wire and arc additive manufacturing
- (2018) J.V. Gordon et al. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
- Anisotropy of fatigue crack growth in wire arc additive manufactured Ti-6Al-4V
- (2018) Yong Xie et al. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
- Additive manufacturing of fatigue resistant materials: Challenges and opportunities
- (2017) Aref Yadollahi et al. INTERNATIONAL JOURNAL OF FATIGUE
- Microstructure, static properties, and fatigue crack growth mechanisms in Ti-6Al-4V fabricated by additive manufacturing: LENS and EBM
- (2016) Yuwei Zhai et al. ENGINEERING FAILURE ANALYSIS
- The formation mechanism of characteristic region at crack initiation for very-high-cycle fatigue of high-strength steels
- (2016) Youshi Hong et al. INTERNATIONAL JOURNAL OF FATIGUE
- Influence of microstructure variability on short crack behavior through postulated micromechanical short crack driving force metrics
- (2015) Andrea Rovinelli et al. ENGINEERING FRACTURE MECHANICS
- A fracture mechanics approach to interior fatigue crack growth in the very high cycle regime
- (2013) Takeshi Ogawa et al. ENGINEERING FRACTURE MECHANICS
- Influence of mean stress and variable amplitude loading on the fatigue behaviour of a high-strength steel in VHCF regime
- (2013) M. Sander et al. INTERNATIONAL JOURNAL OF FATIGUE
- Study of crack initiation or damage in very high cycle fatigue using ultrasonic fatigue test and microstructure analysis
- (2013) Guocai Chai et al. ULTRASONICS
- Application of in situ thermography for evaluating the high-cycle and very high-cycle fatigue behaviour of cast aluminium alloy AlSi7Mg (T6)
- (2013) D. Krewerth et al. ULTRASONICS
- Plasticity and damage heterogeneity in fatigue
- (2007) F. Morel et al. THEORETICAL AND APPLIED FRACTURE MECHANICS
Publish scientific posters with Peeref
Peeref publishes scientific posters from all research disciplines. Our Diamond Open Access policy means free access to content and no publication fees for authors.
Learn MoreCreate your own webinar
Interested in hosting your own webinar? Check the schedule and propose your idea to the Peeref Content Team.
Create Now