Interlaboratory comparison: Round robin test for the damage reproduction of white etching crack in cylindrical roller thrust bearings
Published 2021 View Full Article
- Home
- Publications
- Publication Search
- Publication Details
Title
Interlaboratory comparison: Round robin test for the damage reproduction of white etching crack in cylindrical roller thrust bearings
Authors
Keywords
WEC, White etching crack, WEA, White etching areas, Cylindrical roller thrust bearing, Roller bearings
Journal
WEAR
Volume 480-481, Issue -, Pages 203925
Publisher
Elsevier BV
Online
2021-05-20
DOI
10.1016/j.wear.2021.203925
References
Ask authors/readers for more resources
Related references
Note: Only part of the references are listed.- Hydrogen assisted rolling contact fatigue due to lubricant degradation and formation of white etching areas
- (2019) Dominik Kürten et al. ENGINEERING FAILURE ANALYSIS
- Figure the impact of steel microstructure and heat treatment on the formation of white etching cracks
- (2019) Benjamin Gould et al. TRIBOLOGY INTERNATIONAL
- FE8 type laboratory testing of white etching crack (WEC) bearing failure mode in 100Cr6
- (2019) H.K. Danielsen et al. WEAR
- Effect of lubricants on bearing damage in rolling-sliding conditions: Evolution of white etching cracks
- (2018) Mohanchand Paladugu et al. WEAR
- Threshold Maps for Inclusion-Initiated Micro-Cracks and White Etching Areas in Bearing Steel: The Role of Impact Loading and Surface Sliding
- (2018) T. Bruce et al. TRIBOLOGY LETTERS
- The Effect of Lubricant Composition on White Etching Crack Failures
- (2018) Benjamin Gould et al. TRIBOLOGY LETTERS
- The origins of white etching cracks and their significance to rolling bearing failures
- (2018) Francesco Manieri et al. INTERNATIONAL JOURNAL OF FATIGUE
- Thermal Desorption Analysis of Hydrogen in Non-hydrogen-Charged Rolling Contact Fatigue-Tested 100Cr6 Steel
- (2017) A. D. Richardson et al. TRIBOLOGY LETTERS
- The Evolution of White Etching Cracks (WECs) in Rolling Contact Fatigue-Tested 100Cr6 Steel
- (2017) A. D. Richardson et al. TRIBOLOGY LETTERS
- Reproduction of white etching cracks under rolling contact loading on thrust bearing and two-disc test rigs
- (2017) F. Gutiérrez Guzmán et al. WEAR
- Microstructure deformation and white etching matter formation along cracks
- (2017) Mohanchand Paladugu et al. WEAR
- Microstructural evolution in bearing steel under rolling contact fatigue
- (2017) Shu-Xin Li et al. WEAR
- Multiscale characterization of White Etching Cracks (WEC) in a 100Cr6 bearing from a thrust bearing test rig
- (2017) H.K. Danielsen et al. WEAR
- Bearing performance as a function of structure and heat treatment
- (2016) T. Blass et al. MATERIALS SCIENCE AND TECHNOLOGY
- An updated review: white etching cracks (WECs) and axial cracks in wind turbine gearbox bearings
- (2016) M.-H. Evans MATERIALS SCIENCE AND TECHNOLOGY
- Investigating the Process of White Etching Crack Initiation in Bearing Steel
- (2016) Benjamin Gould et al. TRIBOLOGY LETTERS
- Investigation on the mechanisms of white etching crack (WEC) formation in rolling contact fatigue and identification of a root cause for bearing premature failure
- (2016) Junbiao Lai et al. WEAR
- The Influence of Sliding and Contact Severity on the Generation of White Etching Cracks
- (2015) Benjamin Gould et al. TRIBOLOGY LETTERS
- Confirming subsurface initiation at non-metallic inclusions as one mechanism for white etching crack (WEC) formation
- (2014) M.-H. Evans et al. TRIBOLOGY INTERNATIONAL
- White Etching Crack Root Cause Investigations
- (2014) Walter Holweger et al. TRIBOLOGY TRANSACTIONS
- A FIB/TEM study of butterfly crack formation and white etching area (WEA) microstructural changes under rolling contact fatigue in 100Cr6 bearing steel
- (2013) M.-H. Evans et al. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
- Investigations of Bearing Failures Associated with White Etching Areas (WEAs) in Wind Turbine Gearboxes
- (2013) Robert Errichello et al. TRIBOLOGY TRANSACTIONS
- White structure flaking (WSF) in wind turbine gearbox bearings: effects of ‘butterflies’ and white etching cracks (WECs)
- (2012) M-H Evans MATERIALS SCIENCE AND TECHNOLOGY
- A Comparison of Maximum Likelihood and Median-Rank Regression for Weibull Estimation
- (2010) Ulrike Genschel et al. Quality Engineering
Find Funding. Review Successful Grants.
Explore over 25,000 new funding opportunities and over 6,000,000 successful grants.
ExploreDiscover Peeref hubs
Discuss science. Find collaborators. Network.
Join a conversation