Initiation and Early-Stage Growth of Internal Fatigue Cracking Under Very-High-Cycle Fatigue Regime at High Temperature
Published 2020 View Full Article
- Home
- Publications
- Publication Search
- Publication Details
Title
Initiation and Early-Stage Growth of Internal Fatigue Cracking Under Very-High-Cycle Fatigue Regime at High Temperature
Authors
Keywords
-
Journal
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE
Volume 51, Issue 4, Pages 1575-1592
Publisher
Springer Science and Business Media LLC
Online
2020-02-03
DOI
10.1007/s11661-020-05633-3
References
Ask authors/readers for more resources
Related references
Note: Only part of the references are listed.- Effects of alloying and processing on ultrasonic fatigue behavior in binary Ti-Al alloys
- (2019) Qianying Shi et al. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
- Characterisation of microstructure, defect and high-cycle-fatigue behaviour in a stainless steel joint processed by brazing
- (2019) Y. Li et al. MATERIALS CHARACTERIZATION
- Crystal plasticity assessment of crystallographic Stage I crack propagation in a Ni-based single crystal superalloy
- (2019) Motoki Sakaguchi et al. INTERNATIONAL JOURNAL OF FATIGUE
- The formation of discontinuous gradient regimes during crack initiation in high strength steels under very high cycle fatigue
- (2019) Chengqi Sun et al. INTERNATIONAL JOURNAL OF FATIGUE
- LCF, HCF and VHCF life sensitivity to solution heat treatment of a third-generation Ni-based single crystal superalloy
- (2019) Luciana Maria Bortoluci Ormastroni et al. INTERNATIONAL JOURNAL OF FATIGUE
- Fatigue life and mechanistic modeling of interior micro-defect induced cracking in high cycle and very high cycle regimes
- (2018) Ming-Liang Zhu et al. ACTA MATERIALIA
- Very High Cycle Fatigue of Ni-Based Single-Crystal Superalloys at High Temperature
- (2018) A. Cervellon et al. METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE
- Competing Modes for Crack Initiation from Non-metallic Inclusions and Intrinsic Microstructural Features During Fatigue in a Polycrystalline Nickel-Based Superalloy
- (2018) Jean-Charles Stinville et al. METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE
- Effects of intermittent loading on fatigue life of a high strength steel in very high cycle fatigue regime
- (2018) Chengqi Sun et al. INTERNATIONAL JOURNAL OF FATIGUE
- Microstructure, mechanical properties and cracking behaviour in a γ′-precipitation strengthened nickel-base superalloy fabricated by electron beam melting
- (2018) H. Peng et al. MATERIALS & DESIGN
- VHCF life evolution after microstructure degradation of a Ni-based single crystal superalloy
- (2017) A. Cervellon et al. INTERNATIONAL JOURNAL OF FATIGUE
- Very high cycle fatigue testing of concrete using ultrasonic cycling
- (2017) Ulrike Karr et al. Materials Testing
- A combined grain scale elastic–plastic criterion for identification of fatigue crack initiation sites in a twin containing polycrystalline nickel-base superalloy
- (2016) J.C. Stinville et al. ACTA MATERIALIA
- The effects of heat treatment on very high cycle fatigue behavior in hot-rolled WE43 magnesium
- (2016) Jacob F. Adams et al. INTERNATIONAL JOURNAL OF FATIGUE
- Crack initiation mechanisms of Ti6Al4V in the very high cycle fatigue regime
- (2016) S. Heinz et al. INTERNATIONAL JOURNAL OF FATIGUE
- Crack initiation sensitivity of wrought direct aged alloy 718 in the very high cycle fatigue regime: the role of non-metallic inclusions
- (2016) Damien Texier et al. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
- Benefits of high gradient solidification for creep and low cycle fatigue of AM1 single crystal superalloy
- (2015) S. Steuer et al. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
- Surface vs. interior failure behaviors in a structural steel under gigacycle fatigue: Failure analysis and life prediction
- (2014) Wei Li et al. INTERNATIONAL JOURNAL OF FATIGUE
- Propensities of crack interior initiation and early growth for very-high-cycle fatigue of high strength steels
- (2013) Youshi Hong et al. INTERNATIONAL JOURNAL OF FATIGUE
- Very high cycle fatigue measuring techniques
- (2013) Stefanie Stanzl-Tschegg INTERNATIONAL JOURNAL OF FATIGUE
- Visualization of internal small fatigue crack growth
- (2013) Y. Furuya MATERIALS LETTERS
- Assessment of small fatigue crack growth driving forces in single crystals with and without slip bands
- (2012) Gustavo M. Castelluccio et al. INTERNATIONAL JOURNAL OF FRACTURE
- Diversity of damage evolution during cyclic loading at very high numbers of cycles
- (2012) M Zimmermann INTERNATIONAL MATERIALS REVIEWS
- Subsurface crack initiation and propagation mechanisms in gigacycle fatigue
- (2010) Zhiyong Huang et al. ACTA MATERIALIA
- Small fatigue crack growth and failure mode transitions in a Ni-base superalloy at elevated temperature
- (2010) M.J. Caton et al. INTERNATIONAL JOURNAL OF FATIGUE
- Localized cyclic deformation and corresponding dislocation arrangements of polycrystalline Ni-base superalloys and pure Nickel in the VHCF regime
- (2010) C. Stöcker et al. INTERNATIONAL JOURNAL OF FATIGUE
- Study of thermal effects associated with crack propagation during very high cycle fatigue tests
- (2008) N. Ranc et al. ACTA MATERIALIA
- Fatigue crack growth from small to large cracks on very high cycle fatigue with fish-eye failures
- (2007) Israel Marines-Garcia et al. ENGINEERING FRACTURE MECHANICS
Create your own webinar
Interested in hosting your own webinar? Check the schedule and propose your idea to the Peeref Content Team.
Create NowBecome a Peeref-certified reviewer
The Peeref Institute provides free reviewer training that teaches the core competencies of the academic peer review process.
Get Started