Enhanced tribological properties of PECVD DLC coated thermally sprayed coatings

This research investigates the enhancement of the tribological properties of various thermally-sprayed coatings (APS Ni-50Cr, APS Al2O3-13%TiO, and HVOF WC-17Co) on steel substrate, achieved through the deposition of a thin DLC-based film. Higher adhesive strength between thin films and thermally-sprayed coatings compared to the simple thin film/carbon steel system was found by scratch testing. Dry sliding ball-on-disk tests performed under lower contact pressure conditions (5 N normal load, 6 mm diameter alumina ball) indicated a significant decrease in wear rates and friction coefficients of thermally-sprayed coatings when the thin DLC-based film is employed; little differences exist between the tribological behaviour of the various thin film/thermal spray coating systems and that of DLC-based film on carbon steel. Under higher contact pressure conditions (10 N normal load, 3 mm diameter alumina ball), the thin film/WC-Co system exhibited the best wear performance. These results indicate the superior tribological performance of DLC/thermal spray coating systems, especially under severe contact conditions. (C) 2008 Elsevier B.V. All rights reserved.