5-Methoxy-2-(octadecylthio)benzimidazole (MOTBI) monolayer was self-assembled on fresh copper surface obtained after etching with nitric acid at ambient temperature. The optimum conditions for formation of self-assembled monolayer (SAM) were established using impedance studies. The optimum conditions are methanol as solvent, 10 mM concentration of the organic molecule and an immersion period of 24 h. The MOTBI SAM on copper surface was characterized by contact angle measurements, X-ray photoelectron spectroscopy and reflection absorption FIR spectroscopy and it is inferred that chemisorption of MOTBI on copper surface is through nitrogen. Corrosion protection ability of MOTBI SAM was evaluated in aqueous NaCl solution using impedance, electrochemical quartz crystal nanobalance, potentiodynamic polarization and weight-loss studies. While bare copper showed a charge-transfer resistance (R-ct) value of 1.89 k Omega cm(2) in 0.20 M NaCl aqueous environment, the R-ct value for SAM covered copper surface is 123.4 k Omega cm(2). The MOTBI SAM on copper afforded corrosion inhibition efficiency of 98-99% in NaCl solution in the concentration range and in the temperature range studied. The SAM functions as a cathodic inhibitor. Quantum chemical calculations showed that MOTBI has relatively small Delta E between HOMO and LUMO and large negative charge in its benzimidazole ring, which facilitate formation of a polymeric [Cu+-MOTBI] complex on copper surface. (C) 2009 Elsevier Ltd. All rights reserved.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available