Simple method for the layer-by-layer surface modification of multiwall carbon nanotubes

A simplified method for the surface modification of multiwall carbon nanotubes (MWCNTs) using the layer-by-layer (LbL) technique is proposed. In this approach, the minimum polyelectrolyte content was added to the solution in order to eliminate the tedious centrifugation step. The one pot LbL deposition of poly (diallyldimethylammonium chloride) (PDADMAC), and poly (sodium 4-styrenesulfonate), (PSS) is presented. UV-Vis spectroscopy and zeta potential measurements were used to determine the minimum PDADMAC and PSS concentration needed for the deposition of each polyelectrolyte layer. The deposition cycle was repeated until six layers of PDADMAC/PSS were deposited. The film growth was confirmed by transmission electron microcopy and was found to increase as a function of the number of deposited layers with a final thickness of 18 nm. Evidence of the alternate deposition of oppositely charged polyelectrolytes was further investigated by measurement of the zeta potential values which were found to reverse from positive to negative as a function of the number of deposited layers thus confirming the overcompensation of the surface charge at each adsorption step. This simple method could be useful for the fast preparation of large volumes of MWCNTs solutions in a single batch without the need for centrifugation step. (C) 2011 Elsevier Ltd. All rights reserved.