Utilizing blast furnace slags (BFS) to prepare high-temperature composite phase change materials (C-PCMs)

Blast furnace slag (BFS) is a typical solid waste generated in the steel production. Most of previous investigations have reported that the BFS has been used as traditional construction materials (cement, roadbed filling, concrete). In this study, a novel use route for BFS was proposed to prepare high-temperature composite phase change materials (C-PCMs) for thermal energy storage. Three typical inorganic PCMs (NaN0(3), Al and Na(2)S0(4) with different operating temperature) were blended with the pre-ground BFS to fabricate BFS-based C-PCMs by means of a mixing and sintering process. The results showed that NaN0(3) had excellent chemical compatibility with BFS and the prepared C-PCMs had perfect phase change performance. The enthalpies of NaN0(3)/BFS C-PCMs was 65.53 J/g with melting point 300.5 degrees C and the super-cooling was only 0.1 degrees C Furthermore, the NaN0(3)/BFS C-PCMs could retain good thermal reliability after 100 thermal cycles, which presented a potential application in the thermal energy storage system. In addition, the morphological structure, thermal reliability and heat transfer property of the NaN0(3)/BFS C-PCMs were characterised by using SEM, TGA and TG-DSC. (C) 2018 Elsevier Ltd All rights reserved.