A Search for Low-Irreversible Capacity and High-Reversible Capacity Positive Electrode Materials in the Li-Ni-Mn-Co Pseudoquaternary System

Journal

CHEMISTRY OF MATERIALS
Volume 28, Issue 1, Pages 55-66

Publisher

AMER CHEMICAL SOC
DOI: 10.1021/acs.chemmater.5b02104

Keywords

-

Funding

  1. NSERC
  2. 3M Canada under Industrial Research Chair program

Ask authors/readers for more resources

A comprehensive search for Li-ion battery positive electrode materials that can simultaneously exhibit low irreversible capacity loss (IRC) (similar to 10% or less) and high reversible capacity (>240 mAh/g) was performed in the Li-Ni-Mn-Co-O psendoquaternary system. An array of high-capacity Li-rich layered oxides, most of which show an oxygen release plateau during the first charge, were synthesized with a wide range of Ni, Mn, and Co compositions, and their first-cycle electrochemical properties were investigated. Low-IRC materials could be synthesized at many Ni Mn Co combinations by synthesizing with an amount of lithium lower than that required by site occupation and oxidation state rules. Many of these Li-deficient low-IRC materials were found to be single-phase layered materials with inherent metal-site vacancies in their pristine state. For such single-phase materials, the amount of IRC depends on the concentration of metal-site vacancies in their pristine state. Increasing the Li deficiency eventually caused the appearance of the spinel phase, which, when it appears, lowers the IRC, irrespective of the Ni Mn Co precursor composition. The number of metal-site vacancies that can be incorporated into the single-phase layered materials depends on the overall metal composition, especially the Co concentration. Low-IRC behavior is correlated to the fraction of metal-site vacancies in the layered phase in both the single-phase and the two-phase materials. Li-7 nuclear magnetic resonance (NMR) studies of low-IRC materials revealed the relative population of Li between the Li and TM layer. Formula unit calculation based on Li-7 NMR results suggests that metal-site vacancies preferably occupy the sites in the Li layer, which could provide room for the intercalation of extra Li into the structure, hence reducing the irreversible capacity.

Authors

I am an author on this paper
Click your name to claim this paper and add it to your profile.

Reviews

Primary Rating

4.8
Not enough ratings

Secondary Ratings

Novelty
-
Significance
-
Scientific rigor
-
Rate this paper

Recommended

No Data Available
No Data Available