Effect of hygrothermal aging on the high-temperature interlaminar mechanical properties of CFRP under a complex stress state
Published 2022 View Full Article
- Home
- Publications
- Publication Search
- Publication Details
Title
Effect of hygrothermal aging on the high-temperature interlaminar mechanical properties of CFRP under a complex stress state
Authors
Keywords
-
Journal
JOURNAL OF ADHESION
Volume -, Issue -, Pages 1-31
Publisher
Informa UK Limited
Online
2022-03-21
DOI
10.1080/00218464.2022.2048823
References
Ask authors/readers for more resources
Related references
Note: Only part of the references are listed.- Numerical prediction on the mechanical degradation of adhesively bonded corrugated sandwich beam after hygrothermal ageing
- (2020) Xiao Han et al. COMPOSITE STRUCTURES
- Study on the fracture failure criteria for bonded structures considering temperature sensitivity
- (2020) Jing-Xin Na et al. JOURNAL OF ADHESION SCIENCE AND TECHNOLOGY
- Interlaminar shear property and high-velocity impact resistance of CFRP laminates after cyclic hygrothermal aging
- (2019) Lulu Liu et al. INTERNATIONAL JOURNAL OF CRASHWORTHINESS
- On the fracture behaviour of adhesively bonded CFRP hat-shaped thin-walled beam under axial crushing load: An experimental and modelling study
- (2019) Xiao Han et al. COMPOSITE STRUCTURES
- Material degradation of cfrp-to-steel joints subjected to salt fog
- (2019) Yongming Yang et al. COMPOSITES PART B-ENGINEERING
- Effect of thermal cycling on the degradation of adhesively bonded CFRP/aluminum alloy joints for automobiles
- (2019) Guofeng Qin et al. INTERNATIONAL JOURNAL OF ADHESION AND ADHESIVES
- An experimental investigation of the temperature effect on the mechanics of carbon fiber reinforced polymer composites
- (2018) Zian Jia et al. COMPOSITES SCIENCE AND TECHNOLOGY
- Durability of aluminium alloy adhesive joints in cyclic hydrothermal condition for high-speed EMU applications
- (2018) Guofeng Qin et al. INTERNATIONAL JOURNAL OF ADHESION AND ADHESIVES
- Failure prediction of adhesively bonded CFRP-Aluminum alloy joints using cohesive zone model with consideration of temperature effect
- (2018) Guofeng Qin et al. JOURNAL OF ADHESION
- An updated review of adhesively bonded joints in composite materials
- (2017) S. Budhe et al. INTERNATIONAL JOURNAL OF ADHESION AND ADHESIVES
- Thermal ageing effects on mechanical properties and barely visible impact damage behavior of a carbon fiber reinforced bismaleimide composite
- (2017) Wang Shaoquan et al. MATERIALS & DESIGN
- Analysis on Adhesively-Bonded Joints of FRP-steel Composite Bridge under Combined Loading: Arcan Test Study and Numerical Modeling
- (2016) Xu Jiang et al. Polymers
- Effects of hygrothermal stress on the failure of CFRP composites
- (2015) M. Meng et al. COMPOSITE STRUCTURES
- Experimental study of initial strengths and hygrothermal degradation of adhesive joints between thin aluminum and steel substrates
- (2013) Fan Zhang et al. INTERNATIONAL JOURNAL OF ADHESION AND ADHESIVES
- Effects of adherend thickness and taper on adhesive bond strength measured by portable pull-off tests
- (2013) Mildred Lee et al. INTERNATIONAL JOURNAL OF ADHESION AND ADHESIVES
- Manufacturing Aspects of Advanced Polymer Composites for Automotive Applications
- (2012) Klaus Friedrich et al. APPLIED COMPOSITE MATERIALS
- Experimental and numerical investigation of the static response of environmentally aged adhesively bonded joints
- (2012) S. Sugiman et al. INTERNATIONAL JOURNAL OF ADHESION AND ADHESIVES
- Surface and interface properties of carbon fiber composites under cyclical aging
- (2011) Xinying Lv et al. APPLIED SURFACE SCIENCE
- Effect of temperature and cyclic hygrothermal aging on the interlaminar shear strength of carbon fiber/bismaleimide (BMI) composite
- (2011) Pei Sun et al. MATERIALS & DESIGN
- Tensile Properties of CFRP and Hybrid FRP Composites at Elevated Temperatures
- (2009) Shenghu Cao et al. JOURNAL OF COMPOSITE MATERIALS
- Effects of moisture and UV exposure on liquid molded carbon fabric reinforced nylon 6 composite laminates
- (2008) Selvum Pillay et al. COMPOSITES SCIENCE AND TECHNOLOGY
- Rapid evaluation of long-term thermal degradation of carbon fibre epoxy composites
- (2008) J. Wolfrum et al. COMPOSITES SCIENCE AND TECHNOLOGY
Find Funding. Review Successful Grants.
Explore over 25,000 new funding opportunities and over 6,000,000 successful grants.
ExploreCreate your own webinar
Interested in hosting your own webinar? Check the schedule and propose your idea to the Peeref Content Team.
Create Now