Journal
SUSTAINABILITY
Volume 13, Issue 23, Pages -Publisher
MDPI
DOI: 10.3390/su132313386
Keywords
polypropylene; kinetic analysis; catalytic pyrolysis; bentonite
Funding
- National Research Foundation of Korea (NRF) [NRF-2019R1F1A1061554]
- Technology Innovation Program [20015401]
- Ministry of Trade, Industry & Energy (MOTIE, Korea)
- Korea Environment Industry & Technology Institute (KEITI) through Post Plastic, a specialized program of Graduate School
- Korea Ministry of Environment (MOE)
Ask authors/readers for more resources
This study conducted a kinetic analysis of non-catalytic and catalytic pyrolysis of polypropylene using different catalysts. The use of various catalysts significantly reduced the maximum decomposition temperature and apparent activation energy of PP, with Al-MCM-41 and bentonite having strong acidity and large pore size. Natural zeolite showed lower activation energy at lower conversion rates compared to other catalysts, and a faster increase in activation energy at higher conversion rates.
A kinetic analysis of non-catalytic pyrolysis (NCP) and catalytic pyrolysis (CP) of polypropylene (PP) with different catalysts was performed using thermogravimetric analysis (TGA) and kinetic models. Three kinds of low-cost natural catalysts were used to maximize the cost-effectiveness of the process: natural zeolite (NZ), bentonite, olivine, and a mesoporous catalyst, Al-MCM-41. The decomposition temperature of PP and apparent activation energy (Ea) were obtained from the TGA results at multiple heating rates, and a model-free kinetic analysis was performed using the Flynn-Wall-Ozawa model. TGA indicated that the maximum decomposition temperature (T-max) of the PP was shifted from 464 degrees C to 347 degrees C with Al-MCM-41 and 348 degrees C with bentonite, largely due to their strong acidity and large pore size. Although olivine had a large pore size, the T-max of PP was only shifted to 456 degrees C, because of its low acidity. The differential TG (DTG) curve of PP over NZ revealed a two-step mechanism. The T-max of the first peak on the DTG curve of PP with NZ was 376 degrees C due to the high acidity of NZ. On the other hand, that of the second peak was higher (474 degrees C) than the non-catalytic reaction. The Ea values at each conversion were also decreased when using the catalysts, except olivine. At <0.5 conversion, the Ea obtained from the CP of PP with NZ was lower than that with the other catalysts: Al-MCM-41, bentonite, and olivine, in that order. The Ea for the CP of PP with NZ increased more rapidly, to 193 kJ/mol at 0.9 conversion, than the other catalysts.