The influence of Zn2+ on stress corrosion cracking severity in a highly sensitised Al–Mg alloy

Mitigation of Intergranular Cracking in Al-Mg Alloys via Zn-Based Electrode Potential Control in Sodium Chloride Solution

(2019) Matthew McMahon et al.   CORROSION

The effect of electrode potential on stress corrosion cracking in highly sensitized Al–Mg alloys

(2019) M.E. McMahon et al.   MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING

Mechanistic Studies of Intergranular Stress Corrosion Cracking in Al-Mg Alloys under Atmospheric Exposure Conditions

(2018) Patrick Steiner et al.   CORROSION

Mechanistic Studies of Intergranular Stress Corrosion Cracking in Al-Mg Alloys under Atmospheric Exposure Conditions

(2018) Patrick Steiner et al.   CORROSION

Mitigation of Intergranular Stress Corrosion Cracking in Al–Mg by Electrochemical Potential Control

(2017) M. E. McMahon et al.   JOM

The Effect of Temper and Composition on the Stress Corrosion Cracking of Al-Mg Alloys

(2017) M.E. McMahon et al.   CORROSION

The Effect of Loading Orientation on the Stress Corrosion Cracking of Al-Mg Alloys

(2017) M.E. McMahon et al.   CORROSION

Survey of Detection, Mitigation, and Repair Technologies to Address Problems Caused by Sensitization of Al-Mg Alloys on Navy Ships

(2016) W.J. Golumbfskie et al.   CORROSION

Survey of Detection, Mitigation, and Repair Technologies to Address Problems Caused by Sensitization of Al-Mg Alloys on Navy Ships

(2016) W.J. Golumbfskie et al.   CORROSION

Model to predict intergranular corrosion propagation in three dimensions in AA5083-H131

(2016) Mary Lyn C. Lim et al.   MATERIALS & DESIGN

Modeling sensitization of Al–Mg alloys via β-phase precipitation kinetics

(2015) M.A. Steiner et al.   SCRIPTA MATERIALIA

Measurement and Modeling of Hydrogen Environment-Assisted Cracking in Monel K-500

(2014) Richard P. Gangloff et al.   METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE

Effective Hydrogen Diffusion in Aluminum Alloy 5083-H131 as a Function of Orientation and Degree of Sensitization

(2013) Jia-He Ai et al.   CORROSION

Quantification of Sensitization in AA5083-H131 via Imaging Ga-Embrittled Fracture Surfaces

(2012) N. Birbilis et al.   CORROSION

Intergranular Corrosion Penetration in an Al-Mg Alloy as a Function of Electrochemical and Metallurgical Conditions

(2012) M.L.C. Lim et al.   CORROSION

Spreading of intergranular corrosion on the surface of sensitized Al-4.4Mg alloys: A general finding

(2012) S. Jain et al.   CORROSION SCIENCE

Understanding corrosion via corrosion product characterization: II. Role of alloying elements in improving the corrosion resistance of Zn–Al–Mg coatings on steel

(2011) P. Volovitch et al.   CORROSION SCIENCE

Predicting the Effect of Applied Potential on Crack Tip Hydrogen Concentration in Low-Alloy Martensitic Steels

(2010) B. A. Kehler et al.   CORROSION

Characterization of Inhibitor Release from Zn-Al-[V10O28]6−Hydrotalcite Pigments and Corrosion Protection from Hydrotalcite-Pigmented Epoxy Coatings

(2010) S. P. V. Mahajanam et al.   CORROSION

Understanding corrosion via corrosion product characterization: I. Case study of the role of Mg alloying in Zn–Mg coating on steel

(2009) P. Volovitch et al.   CORROSION SCIENCE