Investigation of co-promotion effect in NiCoMoS/Al2O3 catalysts based on Co2Mo10-heteropolyacid and nickel citrate

Ni(Co)(x)-Co2Mo10/Al2O3 catalysts with various (Co+Ni)/(Co + Ni + Mo) atomic ratio (from 0.17 to 0.45) and constant Mo loading (10 wt.%) were synthesised using decamolybdodicobaltate heteropolyacid (Co(2)Mo(10)HPA) and cobalt or nickel citrate. The catalysts were characterised using N-2 physisorption, high-resolution transmission electron microscopy and X-ray photoelectron spectroscopy and tested in the hydrodesulphurisation (HDS) of dibenzothiophene (DBT). It was found that adding the Co(Ni) citrate to CO2Mo10/Al2O3 catalyst significantly altered the active phase morphology. The average slab length increased from 3.0 to 4.1 nm in Co-x-Co2Mo10/Al2O3 catalysts and to 3.6 nm in Ni-x-Co2Mo10/Al2O3 counterparts. The average stacking number of the MoS2 crystallites grew from 1.4 to 2.0 with loading the Co or Ni. Increasing the Co content in the Co-x-CO2Mo10/Al2O3 catalysts decreased the Co percentage in the CoMoS phase and led to the growth of Co fraction in cobalt sulphide. With the increase of Ni content in Ni-x-Co2Mo10/Al2O3 catalysts the Ni percentage in the NiCoMoS phase decreased from 47 to 25 rel.% and the Co percentage in the NiCoMoS phase was constant and equal to similar to 62 rel.%. For both series of the catalysts, activity in DBT HDS passed through maximum at 0.33 of the atomic ratio (Co + Ni)/( Co + Ni + Mo). Nix-Co2Mo10S/Al2O3 catalysts indicated higher rate constants in DBT HDS than Co-x-Co2Mo10S/Al2O3 counterparts at the same metal content. It was concluded that Ni-1-Co2Mo10/Al2O3 sample with minimal Ni/Mo ratio had mixed Ni-Co-Mo sites with high turnover frequencies values. (C) 2015 Elsevier B.V. All rights reserved.