MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
Volume 772, Issue -, Pages -Publisher
ELSEVIER SCIENCE SA
DOI: 10.1016/j.msea.2019.138797
Keywords
Cu-TiO2 composite; Particle reinforcement; Powder metallurgy; Spark plasma sintering
Categories
Funding
- Project to Create Research and Educational Hubs for Innovative Manufacturing in Asia, Osaka University of Special Budget Project of the Ministry of Education, Culture, Sports, Science, and Technology
Ask authors/readers for more resources
The trade-off between strength and ductility has been a dilemma in copper matrix composites. In this work, we introduce a way of strengthening copper matrix composites containing TiO2 nanoparticles with remarkable ductility. The Cu-8wt%TiO2 composites were fabricated using the powder metallurgy route with spark plasma sintering (SPS) for different holding times incorporating hot extrusion. The sintered composites for longer holding times showed an inhomogeneous distribution of large dispersed particles located mostly along the grain boundaries. However, tensile strength was improved compared with pure copper while ductility was reduced. In contrast, after hot extrusion, a homogeneous distribution of reinforcement particles and grain refinement concurrently triggered strong strengthening and enhanced ductility. The contribution of synergistic strengthening mechanisms, i.e. Hall-Petch strengthening, Orowan pinning, dislocation density and load transfer effect, was studied and the key strengthening mechanisms were elucidated. It was found that composite yielding was strongly affected by sintering time, particulate size and interparticle spacing so that HExt-SPS@30min composite presented the excellent yield strength of 290 MPa, about 72% above pure copper.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available