Journal
APPLIED SURFACE SCIENCE
Volume 493, Issue -, Pages 87-93Publisher
ELSEVIER
DOI: 10.1016/j.apsusc.2019.06.284
Keywords
CeO2; Raman spectroscopy; XPS; Oxygen vacancies; Room temperature ferromagnetism; Photocatalytic
Categories
Funding
- Department of Science and Technology, Ministry of Science and Technology under DST-INSPIRE Faculty scheme [DST/INSPIRE/04/2015/003149]
Ask authors/readers for more resources
Present work reports the influence of defects in the form of oxygen vacancies (V-O) on ferromagnetic behaviour and photocatalytic activity of yttrium (Y) doped Ce1-xYxO2-delta (where x = 0, 0.02, 0.03 and 0.05) samples. The confirmation of single phase crystalline nature of synthesized samples was carried out using XRD. Raman spectroscopy measurement explained the occurrence of oxygen vacancies as a defect in as-synthesized nanoparticles due to distortion in local symmetry of oxygen ions around cerium (Ce) ions. Furthermore, XPS and Raman measurements indicate the presence of mixed valence states (Ce3+ & Ce4+) that in turn leads to the formation of new networks (Ce3+-O-Ce4+, Y3+-O-Ce4+ and Ce3+-O-Ce3+). Magnetic measurement reveals that ferromagnetic character induced in Y doped ceria that ascends upon increase in doping concentration. The presence of both Ce3+ and V-O lead to formation of some localized energy levels which may be responsible for red shift in band gap. Photo-degradation of rose bengal dye in a very short period in the presence of UV-light has been examined in this article. Hence, enhancement in ferromagnetic character and improvement in catalytic behaviour on incorporation of rare-earth ions makes CeO2 an excellent multifunctional material with applications in spintronic devices as well as a catalyst in organic dye degradation.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available