Improvement of Microstructure and Mechanical Properties of CoCrCuFeNi High-Entropy Alloys By V Addition

V element had positive effect in improving the strength of many alloys, so it was possible that V had potential to strengthen CoCrCuFeNi high-entropy alloys (HEAs) with face-centered cubic (FCC) crystal structure, which was relatively weak in strength and had outstanding ductility. In this paper, we studied the alloying effect of V on the phase evolution, microstructure and the mechanical properties of the (CoCrCuFeNi)(100-x)V-x (x=0-16, atomic ratio, hereafter in at.%) HEAs systematically. The results showed that V element had capacity to induce sigma phase precipitation. The volume fraction of sigma phase increased from 0 to 12%; the compressive yield stress of (CoCrCuFeNi)(100-x)V-x HEAs increased from 300 to 613MPa with V content increasing from 0 to 16% (atomic ratio, hereafter in at.%). However, the compression fracture strain decreased from 50 to 28%. V addition was beneficial in improving the strength of CoCrCuFeNi HEA, and the increase in sigma phase volume fraction was the key factor for the improvement of the (CoCrCuFeNi)(100-x)V-x HEAs in yield stress.