The dry sliding wear behaviour of a medium carbon steel against an alumina disk was studied in different heat treated conditions. The wear mechanism in the hardened and tempered steel at 30 N and 40N loads involved an initial adhesive wear followed by an intermediate oxidative wear regime and reappearance of the adhesive wear regime on removal of oxide layer. At 45 N load, the mechanism changed to abrasive wear along with the existence of intermediate oxidative wear of shorter duration. On the other hand, at lower (30 N) and higher (45 N) normal loads the wear mechanism in forced air cooled steel consisted of alternate regimes of adhesive wear and oxidative wear. However at 40 N load, the wear mechanism involved an initial oxidative wear regime for a long duration followed by an adhesive wear regime. The hardened and tempered steel with higher initial hardness and strength, exhibited better wear resistance at lower normal loads (30 N and 40 N) than the forced air cooled steel. However, its wear resistance at higher load (45 N) became inferior to the forced air cooled steel due to lesser extent of work hardening, shorter duration of oxidative wear regime and the abrasive wear being operative. (C) 2010 Elsevier B.V. All rights reserved.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available