Bone Regeneration of Hydroxyapatite/Alumina Bilayered Scaffold with 3 mm Passage-Like Medullary Canal in Canine Tibia Model

The aim of this study was to evaluate the bone regeneration of hydroxyapatite (HA)/alumina bilayered scaffold with a 3 mm passagelike medullary canal in a beagle tibia model. A porous HA/alumina scaffold was fabricated using a polymeric template-coating technique. HA/alumina scaffold dimensions were 10 mm in outer diameter, 20 mm in length, and with either a 3 mm passage or no passage. A 20 mm segmental defect was induced using an oscillating saw through the diaphysis of the beagle tibia. The defects of sLx beagles were filled with HA/alumina bilayered scaffolds with a 3 inns passage or without. The segmental defect was fixated using one bone plate and six screws. Bone regeneration within the HA/alumina scaffolds was observed at eight weeks after implantation. The evaluation of bone regeneration within the scaffolds after implantation in a beagle tibia was performed using radiography; computerized tomography (CT), micro-CT, and fluorescence microscopy: New bone successfully formed in the tibia defects treated with 3 inns passage HA/alumina scaffolds compared to without-passage HA/alumina scaffolds. It was concluded that the HA/alumina bilayered scaffold with 3 mm passage-like medullary canal was instrumental in inducing host-scaffold engraftment of the defect as well as distributing the newly formed bone throughout the scaffold at 8 weeks after implantation.