Spray coating of foley urinary catheter by chlorhexidine-loadedpoly(ε-caprolactone) nanospheres: effect of lyoprotectants, characteristics, and antibacterial activity evaluation

In this study, chlorhexidine-loaded poly(epsilon-caprolactone) nanospheres (CHX-NS) were prepared and successfully coated on the urinary catheters. Properties of CHX-NS were evaluated including drug loading content and the nanosphere size. Effects of different lyoprotectants for long-term storage of CHX-NS were also investigated. In vitro release study and antibacterial activity were also conducted using 20 cycles coated-urinary catheters. Results showed that the high-pressure emulsification-solvent evaporation technique provided the drug loading content at 1.14 +/- 0.16% and the size of nanospheres was 152 +/- 37 nm. The suitable lyoprotectant for long-term storage of CHX-NS was sucrose which provided noticeably no aggregation at the degree of reconstitution at 89.95%. The amount of CHX loading on coated catheters was at 4.55 +/- 0.31 mg. Drug release from the coated catheters in artificial urine could be prolonged up to 2 weeks and bacteria proliferation was inhibited up to 14 days. These results suggest that the antimicrobial activity of CHX-NS reduces the adherence of the uropathogens to the catheter surface. Chlorhexidine-loaded polymeric nanospheres were fabricated which can be successfully coated on urinary catheters. These systems have potential use for prolonged antimicrobial applications.