The focus of this paper is the impact of CF4 based plasma etch processes with the additives argon and C4F8 on material properties and geometrical parameters of etched trenches using dense and porous SiCOH. Argon and C4F8 were added to change the radical to ion composition and to shift the carbon to fluorine ratio, respectively. With several techniques, FTIR, spectral ellipsometry and contact angle measurements, modifications in the structure of the materials and their surface conditions were analyzed. To understand the influences of the additives on the plasma conditions, optical emission spectroscopy (OES) and quadrupole mass spectrometry (QMS) were used to estimate the composition of the plasma in situ. For the additive argon, a slightly enhanced etch rate and an increased refractive index due to serious plasma damage for porous SiCOH was observed. At higher At flow rates peaks of Si2O4Hx clusters in the QMS spectra and increased CO and O lines, measured with OES, indicate a higher sputter yield on the SiCOH network. SEM cross-sections show, that argon has no effect on the sidewall geometry of etched trenches. A higher CH/CN line in the OES spectra indicates an enhanced sputter effect of the SiCN films in via bottoms. For C4F8 addition results of spectral ellipsometry show a decreased etch rate and refractive index. Using FTIR the formation of a polymer film on the surface was observed. Higher C-2 lines in the OES spectra are indications of enhanced polymerization efficiency. Finally, the addition of C4F8 decreases the etch rate in the trench sidewalls and therewith assumedly the sidewall damage. (C) 2009 Elsevier B.V. All rights reserved.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available