The effect of ball-milling on the thermal behavior of anatase-doped hematite ceramic system

High energy ball-milling methods were employed in the synthesis of anatase-doped hematite xTiO(2)(a) center dot A (1-x)alpha-Fe(2)O(3) (x = 0.1, 0.5, and 0.9) ceramic system. The thermal behavior of as obtained ceramic system was characterized by simultaneous DSC-TG. The pure anatase phase was found to be stable below 800 A degrees C, but there is a 10.36% mass loss due to the water content. Two exothermic peaks on DSC curves of pure anatase indicate the different crystallization rates. The pure hematite partially decomposed upon heating under argon atmosphere. Ball-milling has a strong effect on the thermal behaviors of both anatase and hematite phases. For x = 0.1 and 0.5, there is gradual Ti substitution of Fe in hematite lattice, and the decomposition of hematite is enhanced due to the smaller particle size after ball-milling. The crystallization of hematite was suppressed as the enthalpy values decreased due to the anatase-hematite solid-solid interaction. For x = 0.9, most of the anatase phase converted to rutile phase after long milling time. The thermal behavior of xTiO(2)(a) center dot A (1-x)alpha-Fe(2)O(3) showed smaller enthalpy value of the hematite transformation to magnetite and anatase crystallization due to the small fraction of hematite phase in the system and hematite-anatase interaction, while the mass loss upon heating increased as a function of milling time due to more water content absorbed by the smaller particle size.