Donor-acceptor pair recombination luminescence from monoclinic Cu2SnS3 thin film

The defect levels in Cu2SnS3 (CTS) were investigated using photoluminescence (PL) spectroscopy. A CTS thin film was prepared on a soda-lime glass/molybdenum substrate by thermal co-evaporation and sulfurization. The crystal structure was determined to be monoclinic, and the compositional ratios of Cu/Sn and S/Metal were determined to be 1.8 and 1.2, respectively. The photon energy of the PL spectra observed from the CTS thin film was lower than that previously reported. All fitted PL peaks were associated with defect related luminescence. The PL peaks observed at 0.843 and 0.867 eV were assigned to donor-acceptor pair recombination luminescence, the thermal activation energies of which were determined to be 22.9 and 24.8 meV, respectively. (C) 2015 AIP Publishing LLC.