Journal
JOURNAL OF THE MECHANICAL BEHAVIOR OF BIOMEDICAL MATERIALS
Volume 28, Issue -, Pages 232-243Publisher
ELSEVIER SCIENCE BV
DOI: 10.1016/j.jmbbm.2013.08.008
Keywords
Magnesium alloy; Biodegradable implants; In vivo test; Osseointegration; Mechanical test
Funding
- Lorenz Boehler Foundation, Vienna, Austria
- Synthes GmbH, Oberdorf, Switzerland
Ask authors/readers for more resources
Magnesium alloys offer great advantages as degradable implant material for pediatric fracture fixation and hold the potential to overcome certain critical shortcomings inherent to currently used degradable (co)polymers. Besides good biocompatibility and appropriate degradation kinetics, sufficient implant anchorage in host bone is critical to prevent implant failure. Bone-implant anchorage of biodegradable magnesium alloys, however, has not yet been related and compared to that of copolymers, their degradable counterparts currently in clinical use. The aim of this study, therefore, was to comparatively assess bone-implant interface strength and the amount of pen-implant bone of a biodegradable magnesium alloy pin (Mg-Y-Nd-HRE) and a self-reinforced copolymeric control (85/15 poly (L-lactic-co-glycolic acid)). To this purpose, push-out testing, microfocus computed tomography (mu CT), histological and scanning electron microscopic examination was performed after 4, 12 and 24 weeks of transcortical implantation in 72 rats. Biomechanical testing revealed significantly higher ultimate shear strength for the magnesium alloy pins than for the copolymeric controls at all 3 timepoints (P <= 0.001 for all comparisons). As evaluated by mu CT, the amount of bone present near the interface and in a wider radius (up to 0.5 mm) around it was higher in the magnesium alloy implants at 4 weeks, without significant differences at 12 and 24 weeks. Histological examination confirmed direct bone-to-implant contact for both implant types. In vivo degradation of implants did not induce any noticeable local or systemic inflammation. This data suggests that the investigated degradable magnesium alloy rod exhibits markedly superior bone-implant interface strength and a greater amount of peri-implant bone than a self-reinforced copolymeric control currently in use; thus it fulfills a crucial prerequisite for its successful clinical deployment as an alternative degradable orthopedic implant material. Further studies, however, are warranted to evaluate the long-term degradation behavior and biocompatibility of the investigated degradable magnesium-based alloy. (C) 2013 Elsevier Ltd. All rights reserved.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available