JOURNAL OF REINFORCED PLASTICS AND COMPOSITES
Volume 29, Issue 5, Pages 725-730Publisher
SAGE PUBLICATIONS LTD
DOI: 10.1177/0731684408100692
Keywords
jute composites; mechanical and electrical properties; water absorption; diffusivity
Categories
Ask authors/readers for more resources
Hydrophilic character of jute fibers was reduced by acrylation of alkali treated fibers. Jute (treated and untreated) composites of mixed matrix material (25 wt% epoxy resin of bisphenol-C (EBC) and 25 wt% bisphenol-C-formaldehyde (BCF) of jute fibers) were prepared by hand lay-up technique at 150 degrees C under 7.6 MPa pressure for 2 h. Tensile strength was found to increase from 44.3 to 63 MPa (42.2%) and flexural strength was found to increase from 56.2 to 64 MPa (13.9%) on alkali treatment and acrylation. Similarly electric strength was found to increase from 0.18 to 0.72 kV/mm (400%) and volume resistivity was found to increase from 4.13 x 10(16) to 5.1 x 10(16) Omega-cm (123.5%). Water absorption of the composites was carried out at room temperature in distilled water and 10% each of aq. HCl and aq. NaCl solutions, and also in boiling water. The equilibrium water uptake is reduced drastically from 17.3-12.3% to 8.8-4.9% on acrylation. Similarly diffusivity was also found to reduce from 5.7-3.9 x 10(-12) m(2) s(-1) to 4.8-2.2 x 10(-12) m(2) s(-1). Drastic reduction in water uptake and diffusivity are due to replacement of hydrophilic hydroxyl groups to hydrophobic vinyl ester groups. No effect of boiling water was observed on the stability of the composites. Saturation time in boiling water was reduced to about 34 and 30 times without any damage to the JEBCF-50 and TJEBCF-50 composites, respectively.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available