Luminescence properties of BaB8O13:Eu under UV and VUV excitation

The phosphor BaB8O13:Eu3+ were synthesized by solid-state reaction, and their luminescent properties were studied under 254 and 147 nm excitation. The excitation spectrum showed two broad bands in the range of 100-300 nm: one was the host lattice absorption with the maxima at 160 rim and the other was Ba-O absorption overlapped with the CT band of Eu3+, which indicated that the energy of the host lattice absorption could be efficiently transferred to the Eu3+. The overlapped bands were tended to separate when monitored by different wavelength, which indicated that at least two Ba2+ sites were available in BaB8O13. The emissions of Eu3+ (612 nm) and Eu2+ (405 m) were both observed in the emission spectra of BaB8O13:Eu3+ under the excitation of either 254 or 147 nm. With the doping concentration of Eu3+ increasing, the 612 nm emission was enhanced while 405 rim, emission was decreased under 254 nm. excitation, which was due to the persistent energy transfer from Eu2+ to Eu3+. While under 147 rim excitation, the 612 run emission was quenched and the 405 rim emission was enhanced. It was concluded that the preferential excitation of Eu2+ under 147 nm excitation was one of the reasons for this facts.