Composites use in the aerospace industry is expanding, in particular carbon fibre reinforced plastics (CFRP) for structural components. Machinability can however be problematic especially when drilling, due to CFRP's inherent anisotropy/in-homogeneity, limited plastic deformation and abrasive characteristics. Following a brief review on composites development and associated machining, the paper outlines experimental results when twist drilling 1.5 mm diameter holes in 3 mm thick CFRP laminate using tungsten carbide (WC) stepped drills. The control variables considered were prepreg type (3 types) and form (unidirectional (UD) and woven), together with drill feed rate (0.2 and 0.4 mm/rev). A full factorial experimental design was used involving 12 tests. Response variables included the number of drilled holes (wear criterion VB(B)max <= 100 mu m), thrust force and torque, together with entry and exit delamination (conventional and adjusted delamination factor values calculated) and hole diameter. Best results were obtained with woven MTM44-1/HTS oven cured material (3750 holes) while the effect of prepreg form on tool life was evident only when operating at the higher level of feed rate. Thrust forces were typically under 125 N with torque values generally below 65 Nmm over the range of operating parameters employed. Finally, the delamination factor (F-d) measured at hole entry and exit ranged between similar to 1.2-1.8 and 1.0-2.1 respectively. (c) 2010 Elsevier B.V. All rights reserved
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available