Growth of large-sized Ce:Y3Al5O12 (Ce:YAG) scintillation crystal by the temperature gradient technique (TGT)

In this work, Ce:YAG crystal with the size of phi 4 in was successfully grown by the TGT method. The optical and scintillation properties of as-grown Ce:YAG crystals were investigated. Three obvious absorption bands at 223, 340 and 460 nm and two weak color-center absorption bands at 296 and 370 nm are observed in as-grown Ce:YAG crystal. Fluorescence with an emission peak at 398 nm is observed due to the color centers, and absorption bands of the color centers can be eliminated by annealing in O-2 or H-2 atmosphere at 1673 K for 24 h. Yellow-green fluorescence centered at 530 nm is found when the crystal was excited at 460 nm and the 530 nm excitation spectrum shows two peaks at 340 and 460 nm. X-ray fluorescence spectrum of as-grown crystal shows three emission peaks at 300, 360 and 530 nm. An average light output of 1360 phe/MeV and a single exponential decay with the decay time constant of 62.97 ns are found in as-grown Ce:YAG crystal. Crown Copyright (C) 2009 Published by Elsevier B.V. All rights reserved.