Enhanced ammonia adsorption on functionalized nanoporous carbons

Nanoporous carbons were synthesized and treated with nitric acid after which the change in their propensities for ammonia adsorption was determined. The adsorbents had mean pore sizes ranging from 0.5 to 12 nm and they included polyfurfuryl alcohol (PFA)-derived carbons, commercial activated carbons, and both soft and hard-templated mesoporous carbons. The carbons were treated with concentrated nitric acid at elevated temperatures (e.g. 90 degrees C) and for time spans between 15 and 240 min. The textural properties of carbons, before and after nitric acid treatment, were determined using CO2 adsorption at 0 degrees C. Ammonia adsorption uptakes were measured at 25 degrees C and at pressures up to 9.5 bar. The highest total uptake of ammonia on the native carbons, that is prior to nitric acid treatment, was similar to 10 mmol/g at 1 bar and 25 degrees C; this was obtained on a microporous carbon derived from the pyrolysis of polyfurfuryl alcohol and polyethylene glycol blends followed by CO2 oxidation. Nitric acid treatment of this carbon significantly increased its total uptake of ammonia to 17 mmol/g. This sample provided a reversible uptake of 14 mmol/g after it was outgassed at 160 degrees C and 10(-5) bar under dynamic vacuum. This is 2 mmol/g higher than state-of-the-art ammonia adsorbents such as COF-10. An x-ray photoelectron spectrum (XPS) showed that the oxygen content of the carbon increased from 3 at.% to 16.4 at.% after the nitric acid treatment. Heats of adsorption profiles, calculated from adsorption isotherms, started from 165 kJ/mol and quickly dropped to 40 KJ/mol with ammonia loading. This showed that the isosteric heat of adsorption on the remaining surface was still higher than the native carbon sample resulting in high reversible adsorption uptake, even after excluding the irreversible adsorption on the very high energy sites. (C) 2015 Elsevier Inc. All rights reserved.