Broad review of “White Etching Crack” failure in wind turbine gearbox bearings: Main factors and experimental investigations
出版年份 2020 全文链接
标题
Broad review of “White Etching Crack” failure in wind turbine gearbox bearings: Main factors and experimental investigations
作者
关键词
White etching crack, Rolling element bearings, Hydrogen, Non-metallic Inclusions, Microstructural alterations, Sliding/rolling contacts
出版物
INTERNATIONAL JOURNAL OF FATIGUE
Volume 145, Issue -, Pages 106091
出版商
Elsevier BV
发表日期
2020-12-16
DOI
10.1016/j.ijfatigue.2020.106091
参考文献
相关参考文献
注意:仅列出部分参考文献,下载原文获取全部文献信息。- Electrical bearing failures in electric vehicles
- (2020) Feng He et al. Friction
- Material composition and heat treatment related influences in resisting rolling contact fatigue under WEC damage conditions
- (2020) Mohanchand Paladugu et al. INTERNATIONAL JOURNAL OF FATIGUE
- The effect of over-based calcium sulfonate detergent additives on white etching crack (WEC) formation in rolling contact fatigue tested 100Cr6 steel
- (2019) A.D. Richardson et al. TRIBOLOGY INTERNATIONAL
- Influence of raceway surface finish on white etching crack generation in WEC critical oil under rolling-sliding conditions
- (2019) Mohanchand Paladugu et al. WEAR
- Effect of Retained Austenite on White Etching Crack Behavior of Carburized AISI 8620 Steel Under Boundary Lubrication
- (2019) Sougata Roy et al. TRIBOLOGY LETTERS
- The influence of steel microstructure and inclusion characteristics on the formation of premature bearing failures with microstructural alterations
- (2019) Benjamin Gould et al. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
- Hydrogen assisted rolling contact fatigue due to lubricant degradation and formation of white etching areas
- (2019) Dominik Kürten et al. ENGINEERING FAILURE ANALYSIS
- 3D X-ray computerized tomography of White Etching Cracks (WEC)
- (2019) H.K. Danielsen et al. MATERIALS CHARACTERIZATION
- Figure the impact of steel microstructure and heat treatment on the formation of white etching cracks
- (2019) Benjamin Gould et al. TRIBOLOGY INTERNATIONAL
- Finite element simulation of subsurface initiated damage from non-metallic inclusions in wind turbine gearbox bearings
- (2019) Hamza A. Al-Tameemi et al. INTERNATIONAL JOURNAL OF FATIGUE
- Comprehensive analysis of effects of dynamic load frequency and hydrogenation to instigate White Etching Areas (WEAs) formation under severe sliding condition of bearing steel
- (2019) K. Sreeraj et al. TRIBOLOGY INTERNATIONAL
- A unified theory for microstructural alterations in bearing steels under rolling contact fatigue
- (2018) Hanwei Fu et al. ACTA MATERIALIA
- Replication of white etching area evolution using novel modified dynamic load pin-on-disc tribometer on bearing steel
- (2018) K. Sreeraj et al. TRIBOLOGY INTERNATIONAL
- Lubricant Effects on White Etching Cracking Failures in Thrust Bearing Rig Tests
- (2018) Tabassumul Haque et al. TRIBOLOGY TRANSACTIONS
- The Cause of Premature Wind Turbine Bearing Failures: Overloading or Underloading?
- (2018) Nikolay T. Garabedian et al. TRIBOLOGY TRANSACTIONS
- Initiation of sub-surface micro-cracks and white etching areas from debonding at non-metallic inclusions in wind turbine gearbox bearing
- (2018) H.A. Al-Tameemi et al. WEAR
- Effect of lubricants on bearing damage in rolling-sliding conditions: Evolution of white etching cracks
- (2018) Mohanchand Paladugu et al. WEAR
- Formation of white etching areas in SAE 52100 bearing steel under rolling contact fatigue – Influence of diffusible hydrogen
- (2018) M. Oezel et al. WEAR
- Black oxide coating and its effectiveness on prevention of hydrogen uptake
- (2018) S. W. Ooi et al. MATERIALS SCIENCE AND TECHNOLOGY
- The origins of white etching cracks and their significance to rolling bearing failures
- (2018) Francesco Manieri et al. INTERNATIONAL JOURNAL OF FATIGUE
- The predominant role of strain-induced vacancies in hydrogen embrittlement of steels: Overview
- (2018) Michihiko Nagumo et al. ACTA MATERIALIA
- Deformation-induced amorphization and austenitization in white etching area of a martensite bearing steel under rolling contact fatigue
- (2017) Yun-Shuai Su et al. INTERNATIONAL JOURNAL OF FATIGUE
- Electron microscopy investigations of microstructural alterations due to classical Rolling Contact Fatigue (RCF) in martensitic AISI 52100 bearing steel
- (2017) Viktorija Šmeļova et al. INTERNATIONAL JOURNAL OF FATIGUE
- Energy dissipation at rubbing crack faces in rolling contact fatigue as the mechanism of white etching area formation
- (2017) Yuri Kadin et al. INTERNATIONAL JOURNAL OF FATIGUE
- Microstructural changes in White Etching Cracks (WECs) and their relationship with those in Dark Etching Region (DER) and White Etching Bands (WEBs) due to Rolling Contact Fatigue (RCF)
- (2017) Viktorija Šmeļova et al. INTERNATIONAL JOURNAL OF FATIGUE
- Atomic scale characterization of white etching area and its adjacent matrix in a martensitic 100Cr6 bearing steel
- (2017) Y.J. Li et al. MATERIALS CHARACTERIZATION
- Evolution of white-etching cracks and associated microstructural alterations during bearing tests
- (2017) S. W. Ooi et al. MATERIALS SCIENCE AND TECHNOLOGY
- White etching matter promoted by intergranular embrittlement
- (2017) Mohanchand Paladugu et al. SCRIPTA MATERIALIA
- Using advanced tomography techniques to investigate the development of White Etching Cracks in a prematurely failed field bearing
- (2017) Benjamin Gould et al. TRIBOLOGY INTERNATIONAL
- Development of a novel in-situ technique for hydrogen uptake evaluation from a lubricated tribocontact
- (2017) Erfan Abedi Esfahani et al. TRIBOLOGY INTERNATIONAL
- Investigation of Microstructural Alterations in Low- and High-Speed Intermediate-Stage Wind Turbine Gearbox Bearings
- (2017) Harpal Singh et al. TRIBOLOGY LETTERS
- The Effect of Lubricant Additives on Hydrogen Permeation Under Rolling Contact
- (2017) Hiroyoshi Tanaka et al. TRIBOLOGY LETTERS
- Thermal Desorption Analysis of Hydrogen in Non-hydrogen-Charged Rolling Contact Fatigue-Tested 100Cr6 Steel
- (2017) A. D. Richardson et al. TRIBOLOGY LETTERS
- White Etching Cracking—Simulation in Bearing Rig and Bench Tests
- (2017) Joerg Franke et al. TRIBOLOGY TRANSACTIONS
- Microstructure deformation and white etching matter formation along cracks
- (2017) Mohanchand Paladugu et al. WEAR
- Microstructural evolution in bearing steel under rolling contact fatigue
- (2017) Shu-Xin Li et al. WEAR
- Multiscale characterization of White Etching Cracks (WEC) in a 100Cr6 bearing from a thrust bearing test rig
- (2017) H.K. Danielsen et al. WEAR
- An analysis of premature cracking associated with microstructural alterations in an AISI 52100 failed wind turbine bearing using X-ray tomography
- (2017) Benjamin Gould et al. MATERIALS & DESIGN
- Soft novel form of white-etching matter and ductile failure of carbide-free bainitic steels under rolling contact stresses
- (2016) W. Solano-Alvarez et al. ACTA MATERIALIA
- Effects of Electrostatic Discharges on Bearing Grease Dielectric Strength and Composition
- (2016) Aleksei Romanenko et al. IEEE TRANSACTIONS ON INDUSTRY APPLICATIONS
- Predictive Gibbs-energy approach to crystalline/amorphous relative stability of nanoparticles: Size-effect calculations and experimental test
- (2016) J.L. Pelegrina et al. JOURNAL OF ALLOYS AND COMPOUNDS
- Bearing performance as a function of structure and heat treatment
- (2016) T. Blass et al. MATERIALS SCIENCE AND TECHNOLOGY
- An updated review: white etching cracks (WECs) and axial cracks in wind turbine gearbox bearings
- (2016) M.-H. Evans MATERIALS SCIENCE AND TECHNOLOGY
- Electrical pitting of tilting-pad thrust bearings: Modelling and experimental evidence
- (2016) Steven Chatterton et al. TRIBOLOGY INTERNATIONAL
- Fatigue resistant carbon coatings for rolling/sliding contacts
- (2016) Harpal Singh et al. TRIBOLOGY INTERNATIONAL
- Investigating the Process of White Etching Crack Initiation in Bearing Steel
- (2016) Benjamin Gould et al. TRIBOLOGY LETTERS
- Influence of Currents from Electrostatic Charges on WEC Formation in Rolling Bearings
- (2016) Joerg Loos et al. TRIBOLOGY TRANSACTIONS
- WEC Formation in Rolling Bearings under Mixed Friction: Influences and “Friction Energy Accumulation” as Indicator
- (2016) Wolfram Kruhöffer et al. TRIBOLOGY TRANSACTIONS
- Investigation on the mechanisms of white etching crack (WEC) formation in rolling contact fatigue and identification of a root cause for bearing premature failure
- (2016) Junbiao Lai et al. WEAR
- Formation of white etching cracks at manganese sulfide (MnS) inclusions in bearing steel due to hammering impact loading
- (2016) T. Bruce et al. WIND ENERGY
- Observations of the effect of varying Hoop stress on fatigue failure and the formation of white etching areas in hydrogen infused 100Cr6 steel rings
- (2015) Shravan Janakiraman et al. INTERNATIONAL JOURNAL OF FATIGUE
- Critical Assessment 13: Elimination of white etching matter in bearing steels
- (2015) H. K. D. H. Bhadeshia et al. MATERIALS SCIENCE AND TECHNOLOGY
- The Influence of Sliding and Contact Severity on the Generation of White Etching Cracks
- (2015) Benjamin Gould et al. TRIBOLOGY LETTERS
- The Numerical Model of Electrothermal Deformations of Carbides in Bearing Steel as the Possible Cause of White Etching Cracks Initiation
- (2015) Mihails Ščepanskis et al. TRIBOLOGY LETTERS
- Comparison of Black Oxide and Tungsten Carbide–Reinforced Diamond-Like Carbon (WC/a-C:H) Surface Treatments for Rolling Element Bearings
- (2015) Ryan D. Evans et al. TRIBOLOGY TRANSACTIONS
- Friction and wear properties of black oxide surfaces in rolling/sliding contacts
- (2015) Carl H. Hager et al. WEAR
- Characterisation of white etching crack damage in wind turbine gearbox bearings
- (2015) T. Bruce et al. WEAR
- White-Etching Matter in Bearing Steel. Part I: Controlled Cracking of 52100 Steel
- (2014) W. Solano-Alvarez et al. METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE
- White-Etching Matter in Bearing Steel. Part II: Distinguishing Cause and Effect in Bearing Steel Failure
- (2014) W. Solano-Alvarez et al. METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE
- Understanding white etching cracks in rolling element bearings: Formation mechanisms and influent tribochemical drivers
- (2014) Arnaud Ruellan et al. PROCEEDINGS OF THE INSTITUTION OF MECHANICAL ENGINEERS PART J-JOURNAL OF ENGINEERING TRIBOLOGY
- Confirming subsurface initiation at non-metallic inclusions as one mechanism for white etching crack (WEC) formation
- (2014) M.-H. Evans et al. TRIBOLOGY INTERNATIONAL
- White Etching Crack Root Cause Investigations
- (2014) Walter Holweger et al. TRIBOLOGY TRANSACTIONS
- A FIB/TEM study of butterfly crack formation and white etching area (WEA) microstructural changes under rolling contact fatigue in 100Cr6 bearing steel
- (2013) M.-H. Evans et al. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
- White etching crack (WEC) investigation by serial sectioning, focused ion beam and 3-D crack modelling
- (2013) M.-H. Evans et al. TRIBOLOGY INTERNATIONAL
- The Antagonism between Succinimide Dispersants and a Secondary Zinc Dialkyl Dithiophosphate
- (2013) Jie Zhang et al. TRIBOLOGY TRANSACTIONS
- Prevention of Smearing Damage in Cylindrical Roller Bearings
- (2013) Ryan D. Evans et al. TRIBOLOGY TRANSACTIONS
- Investigations of Bearing Failures Associated with White Etching Areas (WEAs) in Wind Turbine Gearboxes
- (2013) Robert Errichello et al. TRIBOLOGY TRANSACTIONS
- Effect of hydrogen on butterfly and white etching crack (WEC) formation under rolling contact fatigue (RCF)
- (2013) M.-H. Evans et al. WEAR
- Material wear and fatigue in wind turbine Systems
- (2013) A. Greco et al. WEAR
- Atomic-scale intermixing, amorphization and microstructural development in a multicomponent system subjected to surface severe plastic deformation
- (2012) S. Romankov et al. ACTA MATERIALIA
- Surface damage on new AS60 rail caused by wheel slip
- (2012) Sarvesh Pal et al. ENGINEERING FAILURE ANALYSIS
- White structure flaking (WSF) in wind turbine gearbox bearings: effects of ‘butterflies’ and white etching cracks (WECs)
- (2012) M-H Evans MATERIALS SCIENCE AND TECHNOLOGY
- Unveiling the nature of hydrogen embrittlement in bearing steels employing a new technique
- (2012) B.A. Szost et al. SCRIPTA MATERIALIA
- Effect of as-ground surface and the BALINIT® C and Nb–S coatings on contact fatigue damage in gears
- (2012) V. Moorthy et al. TRIBOLOGY INTERNATIONAL
- Serial sectioning investigation of butterfly and white etching crack (WEC) formation in wind turbine gearbox bearings
- (2012) M.-H. Evans et al. WEAR
- Effects of plasticity on subsurface initiated spalling in rolling contact fatigue
- (2011) Anurag Warhadpande et al. INTERNATIONAL JOURNAL OF FATIGUE
- Thermal Desorption Analysis of Hydrogen in High Strength Martensitic Steels
- (2011) M. Enomoto et al. METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE
- Steels for bearings
- (2011) H.K.D.H. Bhadeshia PROGRESS IN MATERIALS SCIENCE
- Wear and smearing resistance of black iron mixed oxide coated steels
- (2010) A. Mihailidis et al. International Journal of Surface Science and Engineering
- Tribological advancements for reliable wind turbine performance
- (2010) M. N. Kotzalas et al. PHILOSOPHICAL TRANSACTIONS OF THE ROYAL SOCIETY A-MATHEMATICAL PHYSICAL AND ENGINEERING SCIENCES
- EBSD investigation of the crack initiation and TEM/FIB analyses of the microstructural changes around the cracks formed under Rolling Contact Fatigue (RCF)
- (2009) A. Grabulov et al. INTERNATIONAL JOURNAL OF FATIGUE
- Effects of hydrogen on fatigue crack growth behavior of austenitic stainless steels
- (2008) T KANEZAKI et al. INTERNATIONAL JOURNAL OF HYDROGEN ENERGY
Find Funding. Review Successful Grants.
Explore over 25,000 new funding opportunities and over 6,000,000 successful grants.
ExploreCreate your own webinar
Interested in hosting your own webinar? Check the schedule and propose your idea to the Peeref Content Team.
Create Now