Properties of the Fine Granular Area and Postulated Models for Its Formation during Very High Cycle Fatigue—A Review
出版年份 2020 全文链接
标题
Properties of the Fine Granular Area and Postulated Models for Its Formation during Very High Cycle Fatigue—A Review
作者
关键词
-
出版物
Applied Sciences-Basel
Volume 10, Issue 23, Pages 8475
出版商
MDPI AG
发表日期
2020-11-27
DOI
10.3390/app10238475
参考文献
相关参考文献
注意:仅列出部分参考文献,下载原文获取全部文献信息。- Structure characterization within the vicinity of the fine granular area by synchrotron radiation nano‐CT
- (2020) Long Liu et al. FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES
- Ultrasonic VHCF Tests on Very Large Specimens with Risk-Volume Up to 5000 mm3
- (2020) Andrea Tridello et al. Applied Sciences-Basel
- Influence of cycling frequency and testing volume on the VHCF properties of 18Ni maraging steel
- (2019) Michael Fitzka et al. ENGINEERING FRACTURE MECHANICS
- Initiation and growth behaviour of small internal fatigue cracks in Ti-6Al-4V via synchrotron radiation microcomputed tomography
- (2019) Fumiyoshi Yoshinaka et al. FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES
- The formation of discontinuous gradient regimes during crack initiation in high strength steels under very high cycle fatigue
- (2019) Chengqi Sun et al. INTERNATIONAL JOURNAL OF FATIGUE
- Very high cycle fatigue behavior of bearing steel with rare earth addition
- (2019) Chaoyun Yang et al. INTERNATIONAL JOURNAL OF FATIGUE
- Mechanism of crack initiation and early growth of high strength steels in very high cycle fatigue regime
- (2019) Qingyuan Song et al. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
- Fatigue life and mechanistic modeling of interior micro-defect induced cracking in high cycle and very high cycle regimes
- (2018) Ming-Liang Zhu et al. ACTA MATERIALIA
- The cyclic R-curve – Determination, problems, limitations and application
- (2018) Jürgen Maierhofer et al. ENGINEERING FRACTURE MECHANICS
- A review about the effects of structural and operational factors on the gigacycle fatigue of steels
- (2018) D. Jeddi et al. FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES
- Contributions to the crack initiation mechanisms within the fish eye in Very High Cycle Fatigue regime for steels
- (2018) Chong Wang et al. INTERNATIONAL JOURNAL OF FATIGUE
- On the crystallographic, stage I-like, character of fine granular area formation in internal fish-eye fatigue cracks
- (2018) H. Abdesselam et al. INTERNATIONAL JOURNAL OF FATIGUE
- The role of local plasticity during very high cycle fatigue crack initiation in high-strength steels
- (2018) D. Spriestersbach et al. INTERNATIONAL JOURNAL OF FATIGUE
- Effects of Loading Frequency and Loading Type on High-Cycle and Very-High-Cycle Fatigue of a High-Strength Steel
- (2018) Yuanpei Hu et al. Materials
- Effect of inclusion and microstructure on the very high cycle fatigue behaviors of high strength bainite/martensite multiphase steels
- (2018) Guhui Gao et al. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
- Fracture mechanical characterization of the initiation and growth of interior fatigue cracks
- (2017) S. E. Stanzl-Tschegg FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES
- Influence of mean stress and notches on the very high cycle fatigue behaviour and crack initiation of a low-pressure steam turbine steel
- (2017) F. Ritz et al. FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES
- Effects of inclusions on the very high cycle fatigue behaviour of steels
- (2017) André Pineau et al. FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES
- Reason for the transition of fatigue crack initiation site from surface to subsurface inclusions in high-strength steels
- (2017) P. Grad et al. FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES
- Very high cycle fatigue of cold rolled stainless steels, crack initiation and formation of the fine granular area
- (2017) Muhammad Waqas Tofique et al. INTERNATIONAL JOURNAL OF FATIGUE
- Atomic scale characterization of white etching area and its adjacent matrix in a martensitic 100Cr6 bearing steel
- (2017) Y.J. Li et al. MATERIALS CHARACTERIZATION
- The nature and the mechanism of crack initiation and early growth for very-high-cycle fatigue of metallic materials – An overview
- (2017) Youshi Hong et al. THEORETICAL AND APPLIED FRACTURE MECHANICS
- Mean stress sensitivity and crack initiation mechanisms of spring steel for torsional and axial VHCF loading
- (2016) Herwig Mayer et al. INTERNATIONAL JOURNAL OF FATIGUE
- The formation mechanism of characteristic region at crack initiation for very-high-cycle fatigue of high-strength steels
- (2016) Youshi Hong et al. INTERNATIONAL JOURNAL OF FATIGUE
- Microscopic and nanoscopic study on subsurface damage and fatigue crack initiation during very high cycle fatigue
- (2016) Guocai Chai et al. INTERNATIONAL JOURNAL OF FATIGUE
- Non-destructive observation of internal fatigue crack growth in Ti–6Al–4V by using synchrotron radiation μCT imaging
- (2016) Fumiyoshi Yoshinaka et al. INTERNATIONAL JOURNAL OF FATIGUE
- Very-high-cycle fatigue behavior of a structural steel with and without induced surface defects
- (2016) Qingqing Jiang et al. INTERNATIONAL JOURNAL OF FATIGUE
- Formation of nanosized grain structure in martensitic 100Cr6 bearing steels upon rolling contact loading studied by atom probe tomography
- (2016) Y. J. Li et al. MATERIALS SCIENCE AND TECHNOLOGY
- Very high cycle fatigue of bearing steels with artificial defects in vacuum
- (2016) D. Spriestersbach et al. MATERIALS SCIENCE AND TECHNOLOGY
- Atom Probe Tomography Characterization of a White Etching Area in a Bearing Steel
- (2016) J. Kang et al. MICROSCOPY AND MICROANALYSIS
- Formation of fine grained area in martensitic steel during very high cycle fatigue
- (2015) G. Chai et al. FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES
- A model to predict S–N curves for surface and subsurface crack initiations in different environmental media
- (2015) Guian Qian et al. INTERNATIONAL JOURNAL OF FATIGUE
- Very high cycle fatigue of a high strength steel under sea water corrosion: A strong corrosion and mechanical damage coupling
- (2015) Ruben Pérez-Mora et al. INTERNATIONAL JOURNAL OF FATIGUE
- Effects of stress ratio on high-cycle and very-high-cycle fatigue behavior of a Ti–6Al–4V alloy
- (2015) Xiaolong Liu et al. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
- Experimental study on very high cycle fatigue of martensitic steel of 2Cr13 under corrosive environment
- (2014) S. X. Li et al. FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES
- On specimen design for size effect evaluation in ultrasonic gigacycle fatigue testing
- (2014) D. S. Paolino et al. FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES
- Grain boundary segregation induced strengthening of an ultrafine-grained austenitic stainless steel
- (2014) M.M. Abramova et al. MATERIALS LETTERS
- Mechanisms and modeling of subsurface fatigue cracking in metals
- (2013) A.A. Shanyavskiy ENGINEERING FRACTURE MECHANICS
- A fracture mechanics approach to interior fatigue crack growth in the very high cycle regime
- (2013) Takeshi Ogawa et al. ENGINEERING FRACTURE MECHANICS
- Influence of mean stresses on fatigue life and damage of a turbine blade steel in the VHCF-regime
- (2013) S. Kovacs et al. INTERNATIONAL JOURNAL OF FATIGUE
- Influence of hydrogen content and microstructure on the fatigue behaviour of steel SAE 52100 in the VHCF regime
- (2013) T. Karsch et al. INTERNATIONAL JOURNAL OF FATIGUE
- Modified NASGRO equation for physically short cracks
- (2013) J. Maierhofer et al. INTERNATIONAL JOURNAL OF FATIGUE
- Propensities of crack interior initiation and early growth for very-high-cycle fatigue of high strength steels
- (2013) Youshi Hong et al. INTERNATIONAL JOURNAL OF FATIGUE
- 3D analysis of micro-deformation in VHCF-loaded nodular cast iron by μCT
- (2013) G. Fischer et al. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
- Solute redistribution in the nanocrystalline structure formed in bearing steels
- (2013) J.-H. Kang et al. SCRIPTA MATERIALIA
- Analysis of fatigue properties and failure mechanisms of Ti6Al4V in the very high cycle fatigue regime using ultrasonic technology and 3D laser scanning vibrometry
- (2013) Stefan Heinz et al. ULTRASONICS
- Grain Boundary Segregation in UFG Alloys Processed by Severe Plastic Deformation
- (2012) Xavier Sauvage et al. ADVANCED ENGINEERING MATERIALS
- Fatigue crack propagation properties of Ti–6Al–4V in vacuum environments
- (2012) H. Oguma et al. INTERNATIONAL JOURNAL OF FATIGUE
- Mechanism of fatigue crack initiation and propagation in the very high cycle fatigue regime of high-strength steels
- (2012) P. Grad et al. SCRIPTA MATERIALIA
- Local plasticity exhaustion in a very high cycle fatigue regime
- (2012) Guocai Chai et al. SCRIPTA MATERIALIA
- Effects of strength level and loading frequency on very-high-cycle fatigue behavior for a bearing steel
- (2011) Aiguo Zhao et al. INTERNATIONAL JOURNAL OF FATIGUE
- Notable size effects on very high cycle fatigue properties of high-strength steel
- (2011) Yoshiyuki Furuya MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
- Effect of loading type on fatigue properties of high strength bearing steel in very high cycle regime
- (2011) W. Li et al. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
- Fatigue crack initiation and growth on a steel in the very high cycle regime with sea water corrosion
- (2010) Thierry Palin-Luc et al. ENGINEERING FRACTURE MECHANICS
- On the fatigue crack growth–microstructure relationship in ultrafine-grained interstitial-free steel
- (2010) T. Niendorf et al. JOURNAL OF MATERIALS SCIENCE
- Gigacycle Fatigue Properties of Hydrogen-Charged JIS-SCM440 Low-Alloy Steel Under Ultrasonic Fatigue Testing
- (2010) Yoshiyuki Furuya et al. METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE
- Very high cycle fatigue properties of bainitic high carbon–chromium steel under variable amplitude conditions
- (2009) H. Mayer et al. INTERNATIONAL JOURNAL OF FATIGUE
- Mechanisms of strain localization, crack initiation and fracture of polycrystalline copper in the VHCF regime
- (2009) Stefanie E. Stanzl-Tschegg et al. INTERNATIONAL JOURNAL OF FATIGUE
- Effect of loading condition on very high cycle fatigue behavior in a high strength steel
- (2009) Masaki Nakajima et al. INTERNATIONAL JOURNAL OF FATIGUE
- Fatigue strength of spring steel under axial and torsional loading in the very high cycle regime
- (2008) Y AKINIWA et al. INTERNATIONAL JOURNAL OF FATIGUE
- Very high cycle fatigue properties of bearing steel under axial loading condition
- (2008) K. Shiozawa et al. INTERNATIONAL JOURNAL OF FATIGUE
- Effect of Frequency, Environment, and Temperature on Fatigue Behavior of E319 Cast Aluminum Alloy: Stress-Controlled Fatigue Life Response
- (2008) X. Zhu et al. METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE
- Specimen size effects on gigacycle fatigue properties of high-strength steel under ultrasonic fatigue testing
- (2008) Y. Furuya SCRIPTA MATERIALIA
- Estimation of the size of GBF area on fracture surface for high strength steels in very high cycle fatigue regime
- (2007) Z YANG et al. INTERNATIONAL JOURNAL OF FATIGUE
- Effect of microstructure on ultra-high cycle fatigue behavior of Ti–6Al–4V
- (2007) J.H. Zuo et al. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
Find Funding. Review Successful Grants.
Explore over 25,000 new funding opportunities and over 6,000,000 successful grants.
ExploreBecome a Peeref-certified reviewer
The Peeref Institute provides free reviewer training that teaches the core competencies of the academic peer review process.
Get Started