Structure characterization within the vicinity of the fine granular area by synchrotron radiation nano‐CT
出版年份 2020 全文链接
标题
Structure characterization within the vicinity of the fine granular area by synchrotron radiation nano‐CT
作者
关键词
-
出版物
FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES
Volume -, Issue -, Pages -
出版商
Wiley
发表日期
2020-05-12
DOI
10.1111/ffe.13255
参考文献
相关参考文献
注意:仅列出部分参考文献,下载原文获取全部文献信息。- Initiation and growth behaviour of small internal fatigue cracks in Ti-6Al-4V via synchrotron radiation microcomputed tomography
- (2019) Fumiyoshi Yoshinaka et al. FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES
- In situ synchrotron ultrasonic fatigue testing device for 3D characterisation of internal crack initiation and growth
- (2019) Alexandre Messager et al. FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES
- FGA formation mechanism for X10CrNiMoV12-2-2 and 34CrNiMo6 for constant and variable amplitude tests under the influence of applied mean loads
- (2018) F. Ritz et al. FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES
- Crack growth rates and microstructure feature of initiation region for very-high-cycle fatigue of a high-strength steel
- (2018) Yuanpei Hu et al. FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES
- Pore structure characterization of coal by synchrotron radiation nano-CT
- (2018) Yixin Zhao et al. FUEL
- Very high cycle fatigue of surface carburized CrNi steel at variable stress ratio: Failure analysis and life prediction
- (2018) Abdelhak Nehila et al. INTERNATIONAL JOURNAL OF FATIGUE
- The behavior of crack initiation and early growth in high-cycle and very-high-cycle fatigue regimes for a titanium alloy
- (2018) Xiangnan Pan et al. INTERNATIONAL JOURNAL OF FATIGUE
- On the crystallographic, stage I-like, character of fine granular area formation in internal fish-eye fatigue cracks
- (2018) H. Abdesselam et al. INTERNATIONAL JOURNAL OF FATIGUE
- The role of local plasticity during very high cycle fatigue crack initiation in high-strength steels
- (2018) D. Spriestersbach et al. INTERNATIONAL JOURNAL OF FATIGUE
- Propagation topography of redox phase transformations in heterogeneous layered oxide cathode materials
- (2018) Linqin Mu et al. Nature Communications
- Reason for the transition of fatigue crack initiation site from surface to subsurface inclusions in high-strength steels
- (2017) P. Grad et al. FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES
- ECCI/EBSD and TEM analysis of plastic fatigue damage accumulation responsible for fatigue crack initiation and propagation in VHCF of duplex stainless steels
- (2017) M.W. Tofique et al. INTERNATIONAL JOURNAL OF FATIGUE
- The nature and the mechanism of crack initiation and early growth for very-high-cycle fatigue of metallic materials – An overview
- (2017) Youshi Hong et al. THEORETICAL AND APPLIED FRACTURE MECHANICS
- Effect of defect shape on rolling contact fatigue crack initiation and propagation in high strength steel
- (2016) T. Makino et al. INTERNATIONAL JOURNAL OF FATIGUE
- Small crack growth model from low to very high cycle fatigue regime for internal fatigue failure of high strength steel
- (2016) Yoichi Yamashita et al. INTERNATIONAL JOURNAL OF FATIGUE
- The formation mechanism of characteristic region at crack initiation for very-high-cycle fatigue of high-strength steels
- (2016) Youshi Hong et al. INTERNATIONAL JOURNAL OF FATIGUE
- Microscopic and nanoscopic study on subsurface damage and fatigue crack initiation during very high cycle fatigue
- (2016) Guocai Chai et al. INTERNATIONAL JOURNAL OF FATIGUE
- A user-friendly nano-CT image alignment and 3D reconstruction platform based on LabVIEW
- (2015) Sheng-Hao Wang et al. Chinese Physics C
- Microscopic and nanoscopic observations of metallurgical structures around inclusions at interior crack initiation site for a bearing steel in very high-cycle fatigue
- (2015) T. Sakai et al. FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES
- Mechanisms and modeling of subsurface fatigue cracking in metals
- (2013) A.A. Shanyavskiy ENGINEERING FRACTURE MECHANICS
- A 30 nm-resolution hard X-ray microscope with X-ray fluorescence mapping capability at BSRF
- (2012) Qingxi Yuan et al. JOURNAL OF SYNCHROTRON RADIATION
- Mechanism of fatigue crack initiation and propagation in the very high cycle fatigue regime of high-strength steels
- (2012) P. Grad et al. SCRIPTA MATERIALIA
- Estimation of the size of GBF area on fracture surface for high strength steels in very high cycle fatigue regime
- (2007) Z YANG et al. INTERNATIONAL JOURNAL OF FATIGUE
Publish scientific posters with Peeref
Peeref publishes scientific posters from all research disciplines. Our Diamond Open Access policy means free access to content and no publication fees for authors.
Learn MoreBecome a Peeref-certified reviewer
The Peeref Institute provides free reviewer training that teaches the core competencies of the academic peer review process.
Get Started