Ti-6Al-4V alloy; ultra-high cycle fatigue; microstructure; crack initiation
The fatigue behavior of Ti-6Al-4V alloy with the bimodal and basketweave microstructures has been investigated. The results show that the S-N curves of Ti-6Al-4V with both microstructures continuously decrease with increasing the number of cycles to failure and have no horizontal asymptote in the regime of 10(5) to 10(9) cycles. SEM observation of fracture surface indicates that the crack initiation sites abruptly shift from surface to interior of the specimen with decreasing the stress amplitude. It is found that the surface crack initiation mainly results from the machining traces. Nevertheless, most of the internal fatigue cracks initiate in the border region of primary alpha-grains in bimodal microstructure or at alpha-beta interfaces in basketweave microstructure, which induced by inhomogeneity of microstructures and incompatibility of deformation between two phases. The size of the internal crack initiation site was evaluated and the dependence of the fatigue life on the location and size of the initiation sites is discussed. (C) 2007 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据