The Effect of Lubricant Composition on White Etching Crack Failures
作者
关键词
White etching cracks, Bearing failures, Microstructural alterations, Premature fatigue
出版物
TRIBOLOGY LETTERS
Volume 67, Issue 1, Pages -
出版商
Springer Nature
发表日期
2018-11-29
DOI
10.1007/s11249-018-1106-y
参考文献
相关参考文献
注意:仅列出部分参考文献,下载原文获取全部文献信息。- Lubricant Effects on White Etching Cracking Failures in Thrust Bearing Rig Tests
- (2018) Tabassumul Haque et al. TRIBOLOGY TRANSACTIONS
- The Cause of Premature Wind Turbine Bearing Failures: Overloading or Underloading?
- (2018) Nikolay T. Garabedian et al. TRIBOLOGY TRANSACTIONS
- Threshold Maps for Inclusion-Initiated Micro-Cracks and White Etching Areas in Bearing Steel: The Role of Impact Loading and Surface Sliding
- (2018) T. Bruce et al. TRIBOLOGY LETTERS
- The origins of white etching cracks and their significance to rolling bearing failures
- (2018) Francesco Manieri et al. INTERNATIONAL JOURNAL OF FATIGUE
- Deformation-induced amorphization and austenitization in white etching area of a martensite bearing steel under rolling contact fatigue
- (2017) Yun-Shuai Su et al. INTERNATIONAL JOURNAL OF FATIGUE
- Electron microscopy investigations of microstructural alterations due to classical Rolling Contact Fatigue (RCF) in martensitic AISI 52100 bearing steel
- (2017) Viktorija Šmeļova et al. INTERNATIONAL JOURNAL OF FATIGUE
- Microstructural changes in White Etching Cracks (WECs) and their relationship with those in Dark Etching Region (DER) and White Etching Bands (WEBs) due to Rolling Contact Fatigue (RCF)
- (2017) Viktorija Šmeļova et al. INTERNATIONAL JOURNAL OF FATIGUE
- White etching matter promoted by intergranular embrittlement
- (2017) Mohanchand Paladugu et al. SCRIPTA MATERIALIA
- Using advanced tomography techniques to investigate the development of White Etching Cracks in a prematurely failed field bearing
- (2017) Benjamin Gould et al. TRIBOLOGY INTERNATIONAL
- Investigation of Microstructural Alterations in Low- and High-Speed Intermediate-Stage Wind Turbine Gearbox Bearings
- (2017) Harpal Singh et al. TRIBOLOGY LETTERS
- Thermal Desorption Analysis of Hydrogen in Non-hydrogen-Charged Rolling Contact Fatigue-Tested 100Cr6 Steel
- (2017) A. D. Richardson et al. TRIBOLOGY LETTERS
- The Evolution of White Etching Cracks (WECs) in Rolling Contact Fatigue-Tested 100Cr6 Steel
- (2017) A. D. Richardson et al. TRIBOLOGY LETTERS
- Empirical Investigation of Electricity Self-Generation in a Lubricated Sliding–Rolling Contact
- (2017) Mihails Ščepanskis et al. TRIBOLOGY LETTERS
- White Etching Cracking—Simulation in Bearing Rig and Bench Tests
- (2017) Joerg Franke et al. TRIBOLOGY TRANSACTIONS
- Reproduction of white etching cracks under rolling contact loading on thrust bearing and two-disc test rigs
- (2017) F. Gutiérrez Guzmán et al. WEAR
- Microstructure deformation and white etching matter formation along cracks
- (2017) Mohanchand Paladugu et al. WEAR
- Microstructural evolution in bearing steel under rolling contact fatigue
- (2017) Shu-Xin Li et al. WEAR
- Multiscale characterization of White Etching Cracks (WEC) in a 100Cr6 bearing from a thrust bearing test rig
- (2017) H.K. Danielsen et al. WEAR
- An analysis of premature cracking associated with microstructural alterations in an AISI 52100 failed wind turbine bearing using X-ray tomography
- (2017) Benjamin Gould et al. MATERIALS & DESIGN
- An updated review: white etching cracks (WECs) and axial cracks in wind turbine gearbox bearings
- (2016) M.-H. Evans MATERIALS SCIENCE AND TECHNOLOGY
- Investigating the Process of White Etching Crack Initiation in Bearing Steel
- (2016) Benjamin Gould et al. TRIBOLOGY LETTERS
- Influence of Currents from Electrostatic Charges on WEC Formation in Rolling Bearings
- (2016) Joerg Loos et al. TRIBOLOGY TRANSACTIONS
- WEC Formation in Rolling Bearings under Mixed Friction: Influences and “Friction Energy Accumulation” as Indicator
- (2016) Wolfram Kruhöffer et al. TRIBOLOGY TRANSACTIONS
- Formation of white etching cracks at manganese sulfide (MnS) inclusions in bearing steel due to hammering impact loading
- (2016) T. Bruce et al. WIND ENERGY
- The Influence of Sliding and Contact Severity on the Generation of White Etching Cracks
- (2015) Benjamin Gould et al. TRIBOLOGY LETTERS
- Characterisation of white etching crack damage in wind turbine gearbox bearings
- (2015) T. Bruce et al. WEAR
- Effects of wind shear on wind turbine rotor loads and planetary bearing reliability
- (2015) B. J. Gould et al. WIND ENERGY
- White-Etching Matter in Bearing Steel. Part II: Distinguishing Cause and Effect in Bearing Steel Failure
- (2014) W. Solano-Alvarez et al. METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE
- Confirming subsurface initiation at non-metallic inclusions as one mechanism for white etching crack (WEC) formation
- (2014) M.-H. Evans et al. TRIBOLOGY INTERNATIONAL
- White Etching Crack Root Cause Investigations
- (2014) Walter Holweger et al. TRIBOLOGY TRANSACTIONS
- Solute redistribution in the nanocrystalline structure formed in bearing steels
- (2013) J.-H. Kang et al. SCRIPTA MATERIALIA
- White etching crack (WEC) investigation by serial sectioning, focused ion beam and 3-D crack modelling
- (2013) M.-H. Evans et al. TRIBOLOGY INTERNATIONAL
- Effect of hydrogen on butterfly and white etching crack (WEC) formation under rolling contact fatigue (RCF)
- (2013) M.-H. Evans et al. WEAR
- Material wear and fatigue in wind turbine Systems
- (2013) A. Greco et al. WEAR
- White structure flaking (WSF) in wind turbine gearbox bearings: effects of ‘butterflies’ and white etching cracks (WECs)
- (2012) M-H Evans MATERIALS SCIENCE AND TECHNOLOGY
- Serial sectioning investigation of butterfly and white etching crack (WEC) formation in wind turbine gearbox bearings
- (2012) M.-H. Evans et al. WEAR
- Steels for bearings
- (2011) H.K.D.H. Bhadeshia PROGRESS IN MATERIALS SCIENCE
- Tribological advancements for reliable wind turbine performance
- (2010) M. N. Kotzalas et al. PHILOSOPHICAL TRANSACTIONS OF THE ROYAL SOCIETY A-MATHEMATICAL PHYSICAL AND ENGINEERING SCIENCES
- Effect of hydrogen on Mode II fatigue crack behavior of tempered bearing steel and microstructural changes
- (2009) Shinji Fujita et al. INTERNATIONAL JOURNAL OF FATIGUE
- EBSD investigation of the crack initiation and TEM/FIB analyses of the microstructural changes around the cracks formed under Rolling Contact Fatigue (RCF)
- (2009) A. Grabulov et al. INTERNATIONAL JOURNAL OF FATIGUE
Find Funding. Review Successful Grants.
Explore over 25,000 new funding opportunities and over 6,000,000 successful grants.
ExploreAsk a Question. Answer a Question.
Quickly pose questions to the entire community. Debate answers and get clarity on the most important issues facing researchers.
Get Started