The Evolution of White Etching Cracks (WECs) in Rolling Contact Fatigue-Tested 100Cr6 Steel
出版年份 2017 全文链接
标题
The Evolution of White Etching Cracks (WECs) in Rolling Contact Fatigue-Tested 100Cr6 Steel
作者
关键词
White etching cracks, Wind turbine gearbox bearings, White etching area, Rolling contact fatigue, Rolling element bearings, Bearing failure
出版物
TRIBOLOGY LETTERS
Volume 66, Issue 1, Pages -
出版商
Springer Nature
发表日期
2017-11-27
DOI
10.1007/s11249-017-0946-1
参考文献
相关参考文献
注意:仅列出部分参考文献,下载原文获取全部文献信息。- Energy dissipation at rubbing crack faces in rolling contact fatigue as the mechanism of white etching area formation
- (2017) Yuri Kadin et al. INTERNATIONAL JOURNAL OF FATIGUE
- Microstructural changes in White Etching Cracks (WECs) and their relationship with those in Dark Etching Region (DER) and White Etching Bands (WEBs) due to Rolling Contact Fatigue (RCF)
- (2017) Viktorija Šmeļova et al. INTERNATIONAL JOURNAL OF FATIGUE
- White etching matter promoted by intergranular embrittlement
- (2017) Mohanchand Paladugu et al. SCRIPTA MATERIALIA
- Using advanced tomography techniques to investigate the development of White Etching Cracks in a prematurely failed field bearing
- (2017) Benjamin Gould et al. TRIBOLOGY INTERNATIONAL
- Investigation of Microstructural Alterations in Low- and High-Speed Intermediate-Stage Wind Turbine Gearbox Bearings
- (2017) Harpal Singh et al. TRIBOLOGY LETTERS
- Reproduction of white etching cracks under rolling contact loading on thrust bearing and two-disc test rigs
- (2017) F. Gutiérrez Guzmán et al. WEAR
- Multiscale characterization of White Etching Cracks (WEC) in a 100Cr6 bearing from a thrust bearing test rig
- (2017) H.K. Danielsen et al. WEAR
- An analysis of premature cracking associated with microstructural alterations in an AISI 52100 failed wind turbine bearing using X-ray tomography
- (2017) Benjamin Gould et al. MATERIALS & DESIGN
- Study of subsurface initiation mechanism for white etching crack formation
- (2016) Annika M. Diederichs et al. MATERIALS SCIENCE AND TECHNOLOGY
- Elucidating white-etching matter through high-strain rate tensile testing
- (2016) W. Solano-Alvarez et al. MATERIALS SCIENCE AND TECHNOLOGY
- An updated review: white etching cracks (WECs) and axial cracks in wind turbine gearbox bearings
- (2016) M.-H. Evans MATERIALS SCIENCE AND TECHNOLOGY
- Understanding white etching cracks in rolling element bearings: State of art and multiple driver transposition on a twin-disc machine
- (2016) Arnaud Ruellan et al. PROCEEDINGS OF THE INSTITUTION OF MECHANICAL ENGINEERS PART J-JOURNAL OF ENGINEERING TRIBOLOGY
- Investigating the Process of White Etching Crack Initiation in Bearing Steel
- (2016) Benjamin Gould et al. TRIBOLOGY LETTERS
- WEC Formation in Rolling Bearings under Mixed Friction: Influences and “Friction Energy Accumulation” as Indicator
- (2016) Wolfram Kruhöffer et al. TRIBOLOGY TRANSACTIONS
- Investigation on the mechanisms of white etching crack (WEC) formation in rolling contact fatigue and identification of a root cause for bearing premature failure
- (2016) Junbiao Lai et al. WEAR
- Critical Assessment 13: Elimination of white etching matter in bearing steels
- (2015) H. K. D. H. Bhadeshia et al. MATERIALS SCIENCE AND TECHNOLOGY
- The Influence of Sliding and Contact Severity on the Generation of White Etching Cracks
- (2015) Benjamin Gould et al. TRIBOLOGY LETTERS
- The Numerical Model of Electrothermal Deformations of Carbides in Bearing Steel as the Possible Cause of White Etching Cracks Initiation
- (2015) Mihails Ščepanskis et al. TRIBOLOGY LETTERS
- Characterisation of white etching crack damage in wind turbine gearbox bearings
- (2015) T. Bruce et al. WEAR
- White-Etching Matter in Bearing Steel. Part II: Distinguishing Cause and Effect in Bearing Steel Failure
- (2014) W. Solano-Alvarez et al. METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE
- Formation mechanisms of white etching cracks and white etching area under rolling contact fatigue
- (2014) M-H Evans et al. PROCEEDINGS OF THE INSTITUTION OF MECHANICAL ENGINEERS PART J-JOURNAL OF ENGINEERING TRIBOLOGY
- Confirming subsurface initiation at non-metallic inclusions as one mechanism for white etching crack (WEC) formation
- (2014) M.-H. Evans et al. TRIBOLOGY INTERNATIONAL
- White Etching Crack Root Cause Investigations
- (2014) Walter Holweger et al. TRIBOLOGY TRANSACTIONS
- A FIB/TEM study of butterfly crack formation and white etching area (WEA) microstructural changes under rolling contact fatigue in 100Cr6 bearing steel
- (2013) M.-H. Evans et al. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
- Application of Complementary Techniques for Advanced Characterization of White Etching Cracks
- (2013) O. H. E. West et al. PRAKTISCHE METALLOGRAPHIE-PRACTICAL METALLOGRAPHY
- White etching crack (WEC) investigation by serial sectioning, focused ion beam and 3-D crack modelling
- (2013) M.-H. Evans et al. TRIBOLOGY INTERNATIONAL
- Effect of hydrogen on butterfly and white etching crack (WEC) formation under rolling contact fatigue (RCF)
- (2013) M.-H. Evans et al. WEAR
- Material wear and fatigue in wind turbine Systems
- (2013) A. Greco et al. WEAR
- Non‐destructive subsurface damage monitoring in bearings failure mode using fractal dimension analysis
- (2012) Walter Holweger et al. INDUSTRIAL LUBRICATION AND TRIBOLOGY
- White structure flaking (WSF) in wind turbine gearbox bearings: effects of ‘butterflies’ and white etching cracks (WECs)
- (2012) M-H Evans MATERIALS SCIENCE AND TECHNOLOGY
- A fracture mechanics interpretation of rolling bearing fatigue
- (2012) MWJ Lewis et al. PROCEEDINGS OF THE INSTITUTION OF MECHANICAL ENGINEERS PART J-JOURNAL OF ENGINEERING TRIBOLOGY
- Unveiling the nature of hydrogen embrittlement in bearing steels employing a new technique
- (2012) B.A. Szost et al. SCRIPTA MATERIALIA
- Serial sectioning investigation of butterfly and white etching crack (WEC) formation in wind turbine gearbox bearings
- (2012) M.-H. Evans et al. WEAR
- Effect of hydrogen on Mode II fatigue crack behavior of tempered bearing steel and microstructural changes
- (2009) Shinji Fujita et al. INTERNATIONAL JOURNAL OF FATIGUE
- EBSD investigation of the crack initiation and TEM/FIB analyses of the microstructural changes around the cracks formed under Rolling Contact Fatigue (RCF)
- (2009) A. Grabulov et al. INTERNATIONAL JOURNAL OF FATIGUE
- Über adiabatic shearbands und die Entstehung der „Steilen Weißen Bänder” in Wälzlagern
- (2008) H. Schlicht MATERIALWISSENSCHAFT UND WERKSTOFFTECHNIK
Discover Peeref hubs
Discuss science. Find collaborators. Network.
Join a conversationPublish scientific posters with Peeref
Peeref publishes scientific posters from all research disciplines. Our Diamond Open Access policy means free access to content and no publication fees for authors.
Learn More