ELECTROCHIMICA ACTA
卷 94, 期 -, 页码 277-284出版社
PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.electacta.2013.02.019
关键词
Dye-sensitized solar cells; Chemical dispersion; P25 powder; Transparent electrodes
资金
- [NCET-10-0066]
- [2011RFLXG006]
- [2013AA031502]
A new chemical technique for preparing screen-printing paste from commercially-available P-25 powder was proposed to fabricate TiO2 electrodes for dye-sensitized solar cells (DSSCs). The TiO2 powder and acetic acid were dispersed in ethanol, following that the reactants solutions kept at 80 degrees C for 12 h, then dried in oven for 6 h. This process made the TiO2 particle positively charged and highly dispersed in water. Additionally flocculating reaction using hydrochloric acid was done to change the dispersed TiO2 colloid into viscous paste, which omitted the process of adding polymers as thickener, and kept the purity and porosity of electrodes. The mesoporous transparent TiO2 films about 14 mu m thickness without cracking and peeling-off were fabricated on conducting glass substrates. A high conversion efficiency of 8.07% was obtained under 100 mW cm(-2) AM 1.5 illumination. (C) 2013 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据