Lithium iron phosphate; Mg and F co-doping; Rate performance; Low temperature
资金
- Shanghai Nanotechnology Special Foundation [11nm0500900]
- Shanghai Leading Academic Discipline Project [B502]
- Shanghai Key Laboratory Project [08DZ2230500]
The olivine-type magnesium and fluorine co-doped LiFe0.92Mg0.08(PO4)(0.99)F-0.03/C composites were prepared via a simple solid state reaction. The structure and morphology were characterized by XRD, SEM and EDS. The results present that the Mg and F were uniformly doped into the lattice of LiFePO4 without changing the structure and particle sizes. Compared to undoped LiFePO4/C, Mg doped LiFePO4/C and F doped LiFePO4/C, the co-doped LiFePO4/C shows the best electrochemical performance, especially at low temperature. The specific capacity of the LiFe0.92Mg0.08(PO4)(0.99)F-0.03/C is 121, 109, 94 and 74 mAh g(-1) at the discharge rate of 0.1C, 1C, 2C, 5C under the temperature of -20 degrees C. The co-doped sample also shows an outstanding cycling life at elevated temperature, which remains 94% of its initial capacity after 150 cycles at 60 degrees C. The improved electrochemical performance is due to the increased electronic and ionic conductivity by co-doping with Mg and F. (C) 2013 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据