期刊
ELECTROCHIMICA ACTA
卷 54, 期 10, 页码 2748-2753出版社
PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.electacta.2008.11.026
关键词
Tin oxide; Lithium microbatteries; Cycling performance
资金
- Basic Research Project of National Defence [XMDX2008176]
- Key Project Founded by Fujian province, China [20061-10090]
SnOx thin films were prepared by reactive radio frequency magnetron sputtering with different sputtering powers. X-ray photoelectron spectroscopy suggested that all the films have similar chemical stoichiometry as SnO1.5. X-ray diffraction and transmission electro microscopy results showed that crystal size of the SnOx thin films gradually increases with increase of sputtering power from 50 to 150W. Cyclic voltammetry and galvanostatic charge/discharge cycling measurements indicated that the electrochemical properties of SnOx films strongly rely on their crystal sizes as well as surface morphologies. The SnOx film deposited at sputtering power of 120W exhibits the best electrochemical performances. It could deliver a reversible capacity of 670 mu Ah cm(-2) mu m(-1) at 50 mu A cm(-2) in the voltage range of 0.1-1.2 V up to 50 cycles. (C) 2008 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据