Formation mechanisms of white etching cracks and white etching area under rolling contact fatigue
出版年份 2014 全文链接
标题
Formation mechanisms of white etching cracks and white etching area under rolling contact fatigue
作者
关键词
-
出版物
PROCEEDINGS OF THE INSTITUTION OF MECHANICAL ENGINEERS PART J-JOURNAL OF ENGINEERING TRIBOLOGY
Volume 228, Issue 10, Pages 1047-1062
出版商
SAGE Publications
发表日期
2014-03-15
DOI
10.1177/1350650114525363
参考文献
相关参考文献
注意:仅列出部分参考文献,下载原文获取全部文献信息。- A FIB/TEM study of butterfly crack formation and white etching area (WEA) microstructural changes under rolling contact fatigue in 100Cr6 bearing steel
- (2013) M.-H. Evans et al. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
- White etching crack (WEC) investigation by serial sectioning, focused ion beam and 3-D crack modelling
- (2013) M.-H. Evans et al. TRIBOLOGY INTERNATIONAL
- Investigations of Bearing Failures Associated with White Etching Areas (WEAs) in Wind Turbine Gearboxes
- (2013) Robert Errichello et al. TRIBOLOGY TRANSACTIONS
- Effect of hydrogen on butterfly and white etching crack (WEC) formation under rolling contact fatigue (RCF)
- (2013) M.-H. Evans et al. WEAR
- Material wear and fatigue in wind turbine Systems
- (2013) A. Greco et al. WEAR
- White structure flaking (WSF) in wind turbine gearbox bearings: effects of ‘butterflies’ and white etching cracks (WECs)
- (2012) M-H Evans MATERIALS SCIENCE AND TECHNOLOGY
- A fracture mechanics interpretation of rolling bearing fatigue
- (2012) MWJ Lewis et al. PROCEEDINGS OF THE INSTITUTION OF MECHANICAL ENGINEERS PART J-JOURNAL OF ENGINEERING TRIBOLOGY
- Unveiling the nature of hydrogen embrittlement in bearing steels employing a new technique
- (2012) B.A. Szost et al. SCRIPTA MATERIALIA
- Serial sectioning investigation of butterfly and white etching crack (WEC) formation in wind turbine gearbox bearings
- (2012) M.-H. Evans et al. WEAR
- Thermal Desorption Analysis of Hydrogen in High Strength Martensitic Steels
- (2011) M. Enomoto et al. METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE
- Effect of hydrogen on Mode II fatigue crack behavior of tempered bearing steel and microstructural changes
- (2009) Shinji Fujita et al. INTERNATIONAL JOURNAL OF FATIGUE
- EBSD investigation of the crack initiation and TEM/FIB analyses of the microstructural changes around the cracks formed under Rolling Contact Fatigue (RCF)
- (2009) A. Grabulov et al. INTERNATIONAL JOURNAL OF FATIGUE
- Lattice defects dominating hydrogen-related failure of metals
- (2008) K. Takai et al. ACTA MATERIALIA
- Hydrogen Embrittlement Mechanism in Fatigue of Austenitic Stainless Steels
- (2008) Yukitaka Murakami et al. METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE
Discover Peeref hubs
Discuss science. Find collaborators. Network.
Join a conversationFind the ideal target journal for your manuscript
Explore over 38,000 international journals covering a vast array of academic fields.
Search