Performance of Bond Coats Modified by Platinum Group Metals for Applications in Thermal Barrier Coatings
出版年份 2017 全文链接
标题
Performance of Bond Coats Modified by Platinum Group Metals for Applications in Thermal Barrier Coatings
作者
关键词
bond coats, electron, microscopy, oxidation, platinum group metals, superalloys, thermal barrier coatings
出版物
JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE
Volume 26, Issue 7, Pages 3191-3203
出版商
Springer Nature
发表日期
2017-06-07
DOI
10.1007/s11665-017-2749-9
参考文献
相关参考文献
注意:仅列出部分参考文献,下载原文获取全部文献信息。- Influences of Superalloy Composition and Pt Content on the Oxidation Behavior of Gamma–Gamma Prime NiPtAl Bond Coatings
- (2016) J. A. Haynes et al. OXIDATION OF METALS
- On the performance and failure mechanism of thermal barrier coating systems used in gas turbine blade applications: Influence of bond coat/superalloy combination
- (2015) H.M. Tawancy et al. ENGINEERING FAILURE ANALYSIS
- Enhancing the Oxidation Properties of Gamma Prime + Gamma Platinum Bond Coat by Rhenium and Yttrium Additions for Improved Adhesion of Thermal Barrier Coatings on Nickel-Base Superalloys
- (2015) H. M. Tawancy OXIDATION OF METALS
- Oxidation Behavior of Selected Bond Coats Based on the γ′ + γ Structure and Their Performance in Thermal Barrier Coatings Deposited on a Nickel-Based Superalloy
- (2015) H. M. Tawancy et al. OXIDATION OF METALS
- Influence of Ruthenium on the Oxidation Behavior of Platinum-Rich γ–γ′ Bond Coats and Their Performance in Thermal Barrier Coatings Deposited on a Nickel-Base Superalloy
- (2015) H. M. Tawancy et al. OXIDATION OF METALS
- Correlation of processing technique and microstructure of platinum aluminide bond coats with performance of thermal barrier coatings deposited on nickel base superalloy
- (2014) H. M. Tawancy MATERIALS AT HIGH TEMPERATURES
- Effect of the Superalloy Composition on the Isothermal Oxidation Behaviour of TBC Systems
- (2013) Marion Chieux et al. OXIDATION OF METALS
- On the Degradation Modes and Oxidation Behavior of Platinum Aluminide Bond Coats in Thermal Barrier Coating Used as Surface Protection System for a Turbine Blade Superalloy
- (2013) H. M. Tawancy OXIDATION OF METALS
- Assessment of TBC Oxidation-Induced Degradation Using Compression Tests
- (2013) L. Rémy et al. OXIDATION OF METALS
- Microstructure and high temperature oxidation behavior of Pt-modified aluminide bond coats on Ni-base superalloys
- (2012) D.K. Das PROGRESS IN MATERIALS SCIENCE
- Oxidation failure of TBC systems: An assessment of mechanisms
- (2011) H.E. Evans SURFACE & COATINGS TECHNOLOGY
- Microstructural investigation of PGM-based alloy coatings for oxidation protection
- (2010) Y. Song et al. MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION
- Comparison of the Failures during Cyclic Oxidation of Yttria-Stabilized (7 to 8 Weight Percent) Zirconia Thermal Barrier Coatings Fabricated via Electron Beam Physical Vapor Deposition and Air Plasma Spray
- (2010) N. M. Yanar et al. METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE
- Compositional factors affecting the establishment and maintenance of Al2O3 scales on Ni–Al–Pt systems
- (2009) B. Gleeson et al. JOURNAL OF MATERIALS SCIENCE
Find the ideal target journal for your manuscript
Explore over 38,000 international journals covering a vast array of academic fields.
SearchAsk a Question. Answer a Question.
Quickly pose questions to the entire community. Debate answers and get clarity on the most important issues facing researchers.
Get Started