ISIJ INTERNATIONAL
卷 57, 期 3, 页码 413-419出版社
IRON STEEL INST JAPAN KEIDANREN KAIKAN
DOI: 10.2355/isijinternational.ISIJINT-2016-499
关键词
pre-oxidization; vanadium-titanium magnetite; fluidized bed reduction; structural evolution; MgO migration
资金
- State Key Development Program for Basic Research of China (973 Program) [2013CB632603]
- National Natural Science Foundation of China [21325628, 51404228]
This paper contrastively investigated the reduction behavior of raw and oxidized vanadium titanium magnetite ore (RVTM and OVTM) in a bubbling fluidized bed at 800 degrees C under 75%N2-25%H2, and systematically revealed the relationship between the structure, phases change, MgO migration behavior and the reduction performance. Microstructure observations suggest that oxidization conditions greatly affect structural evolution, phase transformation of Fe Ti oxides, and migration of MgO in OVTM. The reduction results indicated that the average metallization degree enhanced by 8-10% as the OVTM ore had high oxidization degree. When the RVTM ore was treated at 800 degrees C, the reduction rate increased with the increase of oxidization degree, no significant difference was observed among these oxidized samples due to their similar internal and surface structure. However, the reduction rate of OVTM at 950 degrees C depended on the oxidization time. The reduction rate of OVTM oxidized at 950 degrees C for 2 h was faster than the one for 1 h, which was attributed to the better exsolution of MgO and the formation of bigger pores, even though both samples were fully oxidized and Fe2TiO5 formed in the oxidization process.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据