Layered double hydroxide; Intercalation; Composite materials; Thick films; Controlled release
资金
- National Natural Science Foundation of China [21301161]
- 973 Program [2014CB643305]
- Science and Technology Funds from Shinan District of Qingdao [2014-14-016-ZH]
A controlled release method of antifouling agent was demonstrated via the model coating which was fabricated by sodium paeonolsilate (PAS) intercalated into Zn(2)AI Layered Double hydroxides (LDH) and then dispersed in the mixture of acrylic resin and colophony with weight ratio of 2:1. The powder X-ray diffraction (XRD) and Fourier transform infrared spectroscopy (FT-IR) confirm the intercalation of PAS into the galleries of Zn(2)AI-LDH. Some larger particles of Zn(2)AI-PAS-LDH composite in the coating were observed owing to its aggregation, which was revealed by Laser scanning confocal microscope (LSCM). The release tests of the Zn2Al-PAS-LDH coating in 3.5% NaCI solution showed that no burst release phenomenon occurred at the beginning stage and a slower release rate of PAS (0.54 ppm/d) was obtained compared with the pristine PAS coating (1.06 ppm/d), exhibiting its preferable controlled release behavior. The adhesion experiment using Ulva zoospores indicated that Zn2Al-PAS-LDH composite obviously increases the utilization rate of PAS owing to its controlling release property. Therefore, the present work provided a useful strategy to decrease the waste of antifouling agent and prolong the lifetime of antifouling coatings. (C) 2016 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据