Effect of magnetite on physical, tribological and magnetic characteristics of kenaf fibre

The demand for organic fibres with remarkable mechanical, magnetic and physical properties is rising. As a result, the current study investigated the impact of magnetite reinforcement on kenaf fibre. The test samples were prepared by using the hand lay-up process with the addition of magnetite in the range 10-40 wt%. The test results showed that samples with a 30% magnetite content had the best mechanical, physical and tribological characteristics. They showed water absorption of 0 g, average wear of 112 & mu;m and an average frictional force of 1.1 N. The magnetic absorption values of samples with 30 and 40 wt% magnetite were -0.0003 78 to 0.0003 8623 and -0.0002 6021 8 to 0.0002 5781 4 emu/g, respectively.

Automated summary

The impact of magnetite reinforcement on kenaf fibre was investigated, and it was found that samples with 30% magnetite content exhibited the best mechanical, physical, and tribological characteristics.