Effect of pre-hot salt corrosion on hot salt corrosion fatigue behavior of the TC11 titanium alloy at 500 °C
出版年份 2022 全文链接
标题
Effect of pre-hot salt corrosion on hot salt corrosion fatigue behavior of the TC11 titanium alloy at 500 °C
作者
关键词
-
出版物
INTERNATIONAL JOURNAL OF FATIGUE
Volume 163, Issue -, Pages 107055
出版商
Elsevier BV
发表日期
2022-06-03
DOI
10.1016/j.ijfatigue.2022.107055
参考文献
相关参考文献
注意:仅列出部分参考文献,下载原文获取全部文献信息。- High temperature oxidation and hot corrosion behaviors of Ti2AlNb alloy at 923 K and 1023 K
- (2021) Jingjie Dai et al. CORROSION SCIENCE
- Effects of Hot Corrosion on Fatigue Performance of GH4169 Alloy
- (2021) R. Jiang et al. JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE
- Hot Salt Stress Corrosion Cracking Study of Selective Laser Melted Ti-6Al-4V Alloy
- (2021) Mangesh D. Pustode et al. JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE
- AgCl-induced hot salt stress corrosion cracking in a titanium alloy
- (2021) Yitong Shi et al. CORROSION SCIENCE
- Hot corrosion damage mechanism of Ti6Al4V alloy in marine environment
- (2021) Hulin Wu et al. VACUUM
- Effect of plasma electrolytic oxidation on the hot salt corrosion fatigue behavior of the TC17 titanium alloy
- (2021) Hailan Shi et al. MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION
- Degradation mechanism of Ti-6Al-2Sn-4Zr-2Mo-Si alloy exposed to solid NaCl deposit at high temperature
- (2020) Clément Ciszak et al. CORROSION SCIENCE
- Evolution of surface integrity and fatigue properties after milling, polishing, and shot peening of TC17 alloy blades
- (2020) Liang Tan et al. INTERNATIONAL JOURNAL OF FATIGUE
- Corrosion behavior of the resistance sintered TiAl based intermetallics induced by two different molten salt mixture
- (2020) Y. Garip et al. CORROSION SCIENCE
- Pit to crack transition and corrosion fatigue lifetime reduction estimations by means of a short crack microstructural model
- (2020) J.A. Balbín et al. CORROSION SCIENCE
- Stress-corrosion Cracking Susceptibility of Tungsten-inert-gas-welded TC4 Titanium Alloy Joints under Low Strain Rates
- (2019) Yuewei Sun et al. SENSORS AND MATERIALS
- Effect of streaming water vapor on the corrosion behavior of Ti60 alloy under a solid NaCl deposit in water vapor at 600 °C
- (2019) Lei Fan et al. CORROSION SCIENCE
- The mechanisms of hot salt stress corrosion cracking in titanium alloy Ti-6Al-2Sn-4Zr-6Mo
- (2018) Sudha Joseph et al. CORROSION SCIENCE
- Low-temperature hot corrosion effects on the low-cycle fatigue lifetime and cracking behaviors of a powder metallurgy Ni-based superalloy
- (2018) Shaolin Li et al. INTERNATIONAL JOURNAL OF FATIGUE
- Effect of pre hot corrosion on high cycle fatigue behavior of the superalloy IN718 at 600 °C
- (2018) Dhananjay Pradhan et al. INTERNATIONAL JOURNAL OF FATIGUE
- Interaction of hot corrosion fatigue and load dwell periods on a nickel-base single crystal superalloy
- (2018) L. Brooking et al. INTERNATIONAL JOURNAL OF FATIGUE
- Hot corrosion behavior of porous nickel-based alloys containing molybdenum in the presence of NaCl at 750 °C
- (2017) Lingyun Chen et al. ENGINEERING FAILURE ANALYSIS
- NaCl induced corrosion of Ti-6Al-4V alloy at high temperature
- (2016) Clément Ciszak et al. CORROSION SCIENCE
- Understanding the “blue spot”
- (2016) E.A. Saunders et al. ENGINEERING FAILURE ANALYSIS
- Influence of the different salt deposits on the fatigue behavior of a directionally solidified nickel-based superalloy
- (2016) Shaolin Li et al. INTERNATIONAL JOURNAL OF FATIGUE
- Effect of stress ratio on VHCF behavior for a compressor blade titanium alloy
- (2016) Zhi Yong Huang et al. INTERNATIONAL JOURNAL OF FATIGUE
- A continuum damage mechanics model for pit-to-crack transition in AA2024-T3
- (2015) M. Amiri et al. CORROSION SCIENCE
- Effect of high-temperature hot corrosion on the low cycle fatigue behavior of a directionally solidified nickel-base superalloy
- (2015) Xiaoguang Yang et al. INTERNATIONAL JOURNAL OF FATIGUE
- Pit-to-crack transition under cyclic loading in 12% Cr steam turbine blade steel
- (2015) Bernd M. Schönbauer et al. INTERNATIONAL JOURNAL OF FATIGUE
- Hot Salt Stress Corrosion Cracking Behavior of Ti-6242S Alloy
- (2015) Mangesh D. Pustode et al. METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE
- Effect of long term exposure and hydrogen effects on HSSCC behaviour of titanium alloy IMI 834
- (2015) Mangesh D. Pustode et al. MATERIALS & DESIGN
- The stress-corrosion cracking susceptibility of near-α titanium alloy IMI 834 in presence of hot salt
- (2014) Mangesh D. Pustode et al. CORROSION SCIENCE
- Influence of hot corrosion on low cycle fatigue behavior of nickel base superalloy SU 263
- (2013) J.K. Sahu et al. INTERNATIONAL JOURNAL OF FATIGUE
- Effect of hot corrosion on low cycle fatigue behavior of superalloy IN718
- (2013) G.S. Mahobia et al. INTERNATIONAL JOURNAL OF FATIGUE
- Hot Corrosion of Fe-Cr Alloys with 75 Na2SO4 + 25 NaCl Coating at 1173 K
- (2012) Guangyan Fu et al. HIGH TEMPERATURE MATERIALS AND PROCESSES
- The Effects of Hot Corrosion Pits on the Fatigue Resistance of a Disk Superalloy
- (2009) Timothy P. Gabb et al. JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE
- Synergistic corrosion behavior of coated Ti60 alloys with NaCl deposit in moist air at elevated temperature
- (2007) Yuming Xiong et al. CORROSION SCIENCE
Publish scientific posters with Peeref
Peeref publishes scientific posters from all research disciplines. Our Diamond Open Access policy means free access to content and no publication fees for authors.
Learn MoreAsk a Question. Answer a Question.
Quickly pose questions to the entire community. Debate answers and get clarity on the most important issues facing researchers.
Get Started