Pit to crack transition and corrosion fatigue lifetime reduction estimations by means of a short crack microstructural model
出版年份 2020 全文链接
标题
Pit to crack transition and corrosion fatigue lifetime reduction estimations by means of a short crack microstructural model
作者
关键词
Fatigue strength, Pitting corrosion, Pit-to-crack transition, Short cracks, Micromechanical model
出版物
CORROSION SCIENCE
Volume 180, Issue -, Pages 109171
出版商
Elsevier BV
发表日期
2020-12-05
DOI
10.1016/j.corsci.2020.109171
参考文献
相关参考文献
注意：仅列出部分参考文献，下载原文获取全部文献信息。- Most fatal oil & gas pipeline accidents through history: A lessons learned approach
- (2020) M.V. Biezma et al. ENGINEERING FAILURE ANALYSIS
- Predicting fatigue crack initiation from coupled microstructure and corrosion morphology effects
- (2019) Andrea Nicolas et al. ENGINEERING FRACTURE MECHANICS
- Microstructural damage mechanics-based model for creep fracture of 9%Cr steel under prior fatigue loading
- (2019) Wei Zhang et al. THEORETICAL AND APPLIED FRACTURE MECHANICS
- Detecting and imaging stress corrosion cracking in stainless steel, with application to inspecting storage canisters for spent nuclear fuel
- (2019) Marcel C. Remillieux et al. NDT & E INTERNATIONAL
- Progress in developing realistic corrosion models
- (2018) Robert E. Melchers Structure and Infrastructure Engineering
- An efficient procedure for reducing in-line-inspection datasets for structural integrity assessments
- (2018) N.O. Larrosa et al. THEORETICAL AND APPLIED FRACTURE MECHANICS
- Non-propagating cracks in notched components at the fatigue limit analysed with a microstructural model
- (2018) V. Chaves et al. THEORETICAL AND APPLIED FRACTURE MECHANICS
- Pitting corrosion failure analysis of a wet gas pipeline
- (2017) Hamed Mansoori et al. ENGINEERING FAILURE ANALYSIS
- ‘Mind the gap’ in fitness-for-service assessment procedures-review and summary of a recent workshop
- (2017) N.O. Larrosa et al. INTERNATIONAL JOURNAL OF PRESSURE VESSELS AND PIPING
- Corrosion-fatigue: a review of damage tolerance models
- (2017) N. O. Larrosa et al. INTERNATIONAL MATERIALS REVIEWS
- Ultrasonic defect characterization using parametric-manifold mapping
- (2017) A. Velichko et al. PROCEEDINGS OF THE ROYAL SOCIETY A-MATHEMATICAL PHYSICAL AND ENGINEERING SCIENCES
- The influence of corrosion pits on the fatigue life of 17-4PH steam turbine blade steel
- (2015) Bernd M. Schönbauer et al. ENGINEERING FRACTURE MECHANICS
- Short-crack modelling of the effect of corrosion pits on the fatigue limit of 12% Cr steel
- (2015) G. Härkegård FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES
- Calculating fatigue limits of notched components of arbitrary size and shape with cracks growing in mode I
- (2015) N.O. Larrosa et al. INTERNATIONAL JOURNAL OF FATIGUE
- Rapid parametric analysis of SEN(T) specimens using algorithmic modelling: Evaluation of strain energy density and notch stress intensity factors
- (2015) N.O. Larrosa et al. MATERIALS & DESIGN
- Fatigue cracking from a corrosion pit in an aircraft bulkhead
- (2014) S.A. Barter et al. ENGINEERING FAILURE ANALYSIS
- A dislocation based method using generative algorithms to model notch geometries: Determination of Mode I SIFs
- (2014) N.O. Larrosa ENGINEERING FRACTURE MECHANICS
- Mesoscale modeling of microstructurally small fatigue cracks in metallic polycrystals
- (2014) Gustavo M. Castelluccio et al. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
- Data fusion for automated non-destructive inspection
- (2014) N. Brierley et al. PROCEEDINGS OF THE ROYAL SOCIETY A-MATHEMATICAL PHYSICAL AND ENGINEERING SCIENCES
- Corrosion fatigue life prediction of a steel shaft material in seawater
- (2013) Shu-Xin Li et al. ENGINEERING FAILURE ANALYSIS
- Analysis of pitting corrosion on steel under insulation in marine environments
- (2013) Susan Caines et al. JOURNAL OF LOSS PREVENTION IN THE PROCESS INDUSTRIES
- The environmentally small/short crack growth effect: current understanding
- (2012) Alan Turnbull CORROSION REVIEWS
- Fatigue limits for notches of arbitrary profile
- (2012) V. Chaves et al. INTERNATIONAL JOURNAL OF FATIGUE
- Effect of initiation feature on microstructure-scale fatigue crack propagation in Al–Zn–Mg–Cu
- (2011) James T. Burns et al. INTERNATIONAL JOURNAL OF FATIGUE
- New insight into the pit-to-crack transition from finite element analysis of the stress and strain distribution around a corrosion pit
- (2009) A. Turnbull et al. CORROSION SCIENCE
- Effects of dissolved hydrogen and elastic and plastic deformation on active dissolution of pipeline steel in anaerobic groundwater of near-neutral pH
- (2008) B.T. Lu et al. ACTA MATERIALIA
- Application of a microstructural model for predicting notch fatigue limits under mode I loading
- (2008) V. Chaves et al. INTERNATIONAL JOURNAL OF FATIGUE
Find the ideal target journal for your manuscript
Explore over 38,000 international journals covering a vast array of academic fields.
SearchCreate your own webinar
Interested in hosting your own webinar? Check the schedule and propose your idea to the Peeref Content Team.
Create Now