出版年份 2022 全文链接
标题
Effect of cyclic softening and mean stress relaxation on fatigue crack initiation in a hemispherical notch
作者
关键词
-
出版物
FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES
Volume -, Issue -, Pages -
出版商
Wiley
发表日期
2022-09-12
DOI
10.1111/ffe.13834
参考文献
相关参考文献
注意:仅列出部分参考文献,下载原文获取全部文献信息。- Digital image correlation for continuous mapping of fatigue crack initiation sites on corroded surface from offshore mooring chain
- (2021) Paul Qvale et al. INTERNATIONAL JOURNAL OF FATIGUE
- Cyclic behavior and strain energy-based fatigue damage analysis of mooring chains high strength steel
- (2020) Ershad P. Zarandi et al. MARINE STRUCTURES
- Experimental and numerical study of mooring chain residual stresses and implications for fatigue life
- (2020) Ershad P. Zarandi et al. INTERNATIONAL JOURNAL OF FATIGUE
- A novel Strain-Energy-Density based fatigue criterion accounting for mean stress and plasticity effects on the medium-to-high-cycle uniaxial fatigue strength of plain and notched components
- (2019) M. Benedetti et al. INTERNATIONAL JOURNAL OF FATIGUE
- Computational fatigue assessment of mooring chains under tension loading
- (2019) Imanol Martinez Perez et al. ENGINEERING FAILURE ANALYSIS
- High‐strength steel wires containing corrosion pits: stress analysis and critical distance based fatigue life estimation
- (2019) Z. Jie et al. FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES
- Strain evolution around corrosion pits under fatigue loading
- (2018) Christopher Evans et al. THEORETICAL AND APPLIED FRACTURE MECHANICS
- A gradient-based multiaxial criterion for fatigue crack initiation prediction in components with surface roughness
- (2018) Bjørn Skallerud et al. INTERNATIONAL JOURNAL OF FATIGUE
- Review on grinding-induced residual stresses in metallic materials
- (2016) Wenfeng Ding et al. INTERNATIONAL JOURNAL OF ADVANCED MANUFACTURING TECHNOLOGY
- Prediction of surface residual stress after end milling based on cutting force and temperature
- (2016) Yuan Ma et al. JOURNAL OF MATERIALS PROCESSING TECHNOLOGY
- A comparative study of design code criteria for prediction of the fatigue limit under in-phase and out-of-phase tension–torsion cycles
- (2015) Ø.A. Bruun et al. INTERNATIONAL JOURNAL OF FATIGUE
- Differences and similarities between the induced residual stresses after ball end milling and orthogonal cutting of Ti–6Al–4V
- (2015) Dennis Nespor et al. JOURNAL OF MATERIALS PROCESSING TECHNOLOGY
- Analysis of uniaxial ratcheting behavior and cyclic mean stress relaxation of a duplex stainless steel
- (2014) Chin-Hyung Lee et al. INTERNATIONAL JOURNAL OF PLASTICITY
- Cyclic inelastic constitutive equations and their impact on the fatigue life predictions
- (2012) J.-L. Chaboche et al. INTERNATIONAL JOURNAL OF PLASTICITY
- Assessment of methods for prediction of notch and size effects at the fatigue limit based on test data by Böhm and Magin
- (2010) G. Härkegård et al. INTERNATIONAL JOURNAL OF FATIGUE
- Numerical investigation on stress concentration of corrosion pit
- (2009) M. Cerit et al. ENGINEERING FAILURE ANALYSIS
- A comparison of maximum likelihood models for fatigue strength characterization in materials exhibiting a fatigue limit
- (2008) Randall D. Pollak et al. PROBABILISTIC ENGINEERING MECHANICS
Find Funding. Review Successful Grants.
Explore over 25,000 new funding opportunities and over 6,000,000 successful grants.
ExploreCreate your own webinar
Interested in hosting your own webinar? Check the schedule and propose your idea to the Peeref Content Team.
Create Now