Digital image correlation for continuous mapping of fatigue crack initiation sites on corroded surface from offshore mooring chain
出版年份 2021 全文链接
标题
Digital image correlation for continuous mapping of fatigue crack initiation sites on corroded surface from offshore mooring chain
作者
关键词
Fatigue initiation, Digital image correlation, Finite elements, Corrosion fatigue, Offshore engineering
出版物
INTERNATIONAL JOURNAL OF FATIGUE
Volume 151, Issue -, Pages 106350
出版商
Elsevier BV
发表日期
2021-05-28
DOI
10.1016/j.ijfatigue.2021.106350
参考文献
相关参考文献
注意:仅列出部分参考文献,下载原文获取全部文献信息。- Cyclic behavior and strain energy-based fatigue damage analysis of mooring chains high strength steel
- (2020) Ershad P. Zarandi et al. MARINE STRUCTURES
- Waveform and frequency effects on corrosion-fatigue crack growth behaviour in modern marine steels
- (2020) Victor Igwemezie et al. INTERNATIONAL JOURNAL OF FATIGUE
- Experimental and numerical study of mooring chain residual stresses and implications for fatigue life
- (2020) Ershad P. Zarandi et al. INTERNATIONAL JOURNAL OF FATIGUE
- Correlation of laboratory and real marine corrosion for the investigation of corrosion fatigue behaviour of steel components
- (2019) Stefanos Gkatzogiannis et al. INTERNATIONAL JOURNAL OF FATIGUE
- Predicting fatigue crack initiation from coupled microstructure and corrosion morphology effects
- (2019) Andrea Nicolas et al. ENGINEERING FRACTURE MECHANICS
- Computational fatigue assessment of mooring chains under tension loading
- (2019) Imanol Martinez Perez et al. ENGINEERING FAILURE ANALYSIS
- The effect of pit size and density on the fatigue behaviour of a pre-corroded martensitic stainless steel
- (2018) M.D. McMurtrey et al. FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES
- Equivalent surface defect model for fatigue life prediction of steel reinforcing bars with pitting corrosion
- (2018) Jie Chen et al. INTERNATIONAL JOURNAL OF FATIGUE
- Strain evolution around corrosion pits under fatigue loading
- (2018) Christopher Evans et al. THEORETICAL AND APPLIED FRACTURE MECHANICS
- Modeling for corrosion fatigue crack initiation life based on corrosion kinetics and equivalent initial flaw size theory
- (2018) Tianliang Zhao et al. CORROSION SCIENCE
- A gradient-based multiaxial criterion for fatigue crack initiation prediction in components with surface roughness
- (2018) Bjørn Skallerud et al. INTERNATIONAL JOURNAL OF FATIGUE
- In situnear-tip normal strain evolution of a growing fatigue crack
- (2016) M.-L. Zhu et al. FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES
- High resolution digital image correlation measurements of strain accumulation in fatigue crack growth
- (2012) Jay D. Carroll et al. INTERNATIONAL JOURNAL OF FATIGUE
- Measuring discontinuous displacement fields in cracked specimens using digital image correlation with mesh adaptation and crack-path optimization
- (2012) E. Fagerholt et al. OPTICS AND LASERS IN ENGINEERING
- Identification of a crack propagation law by digital image correlation
- (2011) Florent Mathieu et al. INTERNATIONAL JOURNAL OF FATIGUE
- Fatigue microcrack detection with digital image correlation
- (2011) J Rupil et al. JOURNAL OF STRAIN ANALYSIS FOR ENGINEERING DESIGN
- Assessment of methods for prediction of notch and size effects at the fatigue limit based on test data by Böhm and Magin
- (2010) G. Härkegård et al. INTERNATIONAL JOURNAL OF FATIGUE
- Fringe projection techniques: Whither we are?
- (2009) Sai Siva Gorthi et al. OPTICS AND LASERS IN ENGINEERING
- A comparison of maximum likelihood models for fatigue strength characterization in materials exhibiting a fatigue limit
- (2008) Randall D. Pollak et al. PROBABILISTIC ENGINEERING MECHANICS
Discover Peeref hubs
Discuss science. Find collaborators. Network.
Join a conversationAsk a Question. Answer a Question.
Quickly pose questions to the entire community. Debate answers and get clarity on the most important issues facing researchers.
Get Started